Fire and water resistant expansion joint system

1. An expansion joint system, comprising:

foam; and

a fire retardant material dispersed within the foam by infusing the fire retardant material in the foam, the foam with the fire retardant material therein configured to have a compressed density effective to pass testing as provided by UL 2079;

wherein the expansion joint system is configured to facilitate compression of the system between substrates by repeatedly expanding and contracting to accommodate movement of the substrates; and

wherein the foam with the fire retardant material therein is configured to withstand exposure to a temperature of about 540° C. at about five minutes.

2. The expansion joint system of claim 1 , wherein the foam with the fire retardant material has a compressed density in a range of about 200 kg/m 3 to about 700 kg/m 3 .

3. The expansion joint system of claim 1 , wherein the foam with the fire retardant material uncompressed has a density of about 130 kg/m 3 to about 150 kg/m 3 .

4. The expansion joint system of claim 1 , wherein the system is configured to maintain fire resistance upon exposure to a temperature of about 930° C. at about one hour.

5. The expansion joint system of claim 1 , wherein the system is configured to maintain fire resistance upon exposure to a temperature of about 1010° C. at about two hours.

6. The expansion joint system of claim 1 , wherein the ratio of the fire retardant material dispersed within the foam is in a range of about 3.5:1 to about 4:1 by weight.

7. The expansion joint system of claim 1 , wherein the foam comprises open celled polyurethane foam.

8. The expansion joint system of claim 7 , wherein the foam comprises a plurality of laminations of the open celled polyurethane foam.

9. The expansion joint system of claim 1 , wherein the foam with the fire retardant material has a compressed density in a range of about 400 kg/m 3 to about 450 kg/m 3 .

10. The expansion joint system of claim 1 , wherein the fire retardant material dispersed within the foam is selected from the group consisting of metal oxides, metal hydroxides, aluminum oxides, antimony oxides and hydroxides, iron compounds, ferrocene, molybdenum trioxide, nitrogen-based compounds, water-based aluminum tri-hydrate and combinations of the foregoing materials.

11. The expansion joint system of claim 1 , wherein the foam comprises a plurality of laminations, at least one of the laminations has the fire retardant material dispersed therein.

12. The expansion joint system of claim 11 , wherein the lamination having fire retardant dispersed therein is an inner lamination of the plurality of laminations.

13. The expansion joint system of claim 11 , wherein the laminations are oriented, with respect to the direction in which the joint extends in its width, in at least one of a parallel orientation, a perpendicular orientation, and a combination thereof.

14. The expansion joint system of claim 1 , wherein the fire retardant material is dispersed substantially uniform throughout the foam.

15. The expansion joint system of claim 1 , wherein the expansion joint system is capable of withstanding exposure to a temperature of about 1052° C. for about three hours.

16. An expansion joint system, comprising:

foam;

a fire retardant material dispersed within the foam by infusing the fire retardant material in the foam, the foam with the fire retardant material therein configured to have a compressed density effective to pass testing as provided by UL 2079; and

a water resistant layer on the foam;

wherein the expansion joint system is configured to facilitate compression of the system between substrates by repeatedly expanding and contracting to accommodate movement of the substrates; and

wherein the foam with the fire retardant material therein is configured to withstand exposure to a temperature of about 540° C. at about five minutes.

17. The expansion joint system of claim 16 , wherein the foam with the fire retardant material has a compressed density in a range of about 200 kg/m 3 to about 700 kg/m 3 .

18. The expansion joint system of claim 16 , wherein the foam with the fire retardant material uncompressed has a density of about 130 kg/m 3 to about 150 kg/m 3 .

19. The expansion joint system of claim 16 , wherein the foam with the fire retardant material is configured to maintain fire resistance upon exposure to a temperature of about 930° C. at about one hour.

20. The expansion joint system of claim 16 , wherein the foam with the fire retardant material is configured to maintain fire resistance upon exposure to a temperature of about 1010° C. at about two hours.

21. The expansion joint system of claim 16 , wherein the foam and the water resistant layer define a bellows profile.

22. The expansion joint system of claim 16 , wherein the water resistant layer comprises silicone.

23. The expansion joint system of claim 16 , further comprising a fire resistant layer.

24. The expansion joint system of claim 23 , wherein the fire resistant layer is disposed on a surface of the foam and the water resistant layer is disposed on a surface of the foam opposing the fire resistant layer.

25. The expansion joint system of claim 24 , wherein the fire resistant layer and the water resistant layer are configured to define a bellows profile.

26. The expansion joint system of claim 16 further comprising at least one of a sealant band and a corner bead.

27. The expansion joint system of claim 16 , wherein the ratio of the fire retardant material dispersed in the foam is in a range of about 3.5:1 to about 4:1 by weight.

28. The expansion joint system of claim 16 , wherein the foam comprises open celled polyurethane foam.

29. The expansion joint system of claim 28 , wherein the foam comprises a plurality of laminations of the open celled polyurethane foam.

30. The expansion joint system of claim 16 , wherein the foam with the fire retardant material has a compressed density in a range of about 400 kg/m 3 to about 450 kg/m 3 .

31. The expansion joint system of claim 16 , wherein the fire retardant material dispersed within the foam is selected from the group consisting of metal oxides, metal hydroxides, aluminum oxides, antimony oxides and hydroxides, iron compounds, ferrocene, molybdenum trioxide, nitrogen-based compounds, water-based aluminum tri-hydrate and combinations of the foregoing materials.

32. The expansion joint system of claim 16 , wherein the foam comprises a plurality of laminations, at least one of the laminations is dispersed within with the fire retardant material.

33. The expansion joint system of claim 32 , wherein the lamination having fire retardant dispersed therein is an inner lamination of the plurality of laminations.

34. The expansion joint system of claim 32 , wherein the laminations are oriented, with respect to the direction in which the joint extends in its width, in at least one of a parallel orientation, a perpendicular orientation, and a combination thereof.

35. The expansion joint system of claim 16 , wherein the fire retardant material is dispersed substantially uniform throughout the foam.

36. The expansion joint system of claim 16 , wherein the expansion joint system is capable of withstanding exposure to a temperature of about 1052° C. for about three hours.

37. An expansion joint system, comprising:

foam;

a fire retardant material disposed within the foam by infusing the fire retardant material in the foam, the foam with the fire retardant material therein configured to have a compressed density effective to pass testing as provided by UL 2079;

a first layer of an intumescent material disposed on a first surface of the foam; and

a first layer of an elastomer disposed on at least one of a second surface of the foam and the layer of the intumescent material;

wherein the expansion joint system is configured to facilitate compression of the system between substrates to accommodate movement of the substrates; and

wherein the foam with the fire retardant material therein is configured to withstand exposure to a temperature of about 930° C. at about one hour.

38. The expansion joint system of claim 37 , wherein the foam comprises a plurality of laminations of foam.

39. The expansion joint system of claim 37 , wherein the foam is open celled polyurethane foam.

40. The expansion joint system of claim 37 , wherein the fire retardant material disposed in the foam is selected from the group consisting of metal oxides, metal hydroxides, aluminum oxides, antimony oxides and hydroxides, iron compounds, ferrocene, molybdenum trioxide, nitrogen-based compounds, water-based aluminum tri-hydrate and combinations of the foregoing materials.

41. The expansion joint system of claim 37 , wherein the elastomer disposed on the surface of the foam comprises a silicone.

42. The expansion joint system of claim 37 , wherein the elastomer disposed on the surface of the foam is selected from the group consisting of polysulfides, acrylics, polyurethanes, poly-epoxides, silyl-terminated polyethers, and combinations of one or more of the foregoing.

43. The expansion joint system of claim 37 , wherein the intumescent material disposed on the surface of the foam comprises a fire barrier caulk.

44. The expansion joint system of claim 37 , wherein the foam uncompressed has a density of about 130 kg/m 3 to about 150 kg/m 3 .

45. The expansion joint system of claim 37 , wherein the foam with the fire retardant material compressed has a density in a range of about 200 kg/m 3 to about 700 kg/m 3 .

46. The expansion joint system of claim 37 , wherein the foam with the fire retardant material compressed has a density in a range of about 400 kg/m 3 to about 450 kg/m 3 .

47. The expansion joint system of claim 37 , further comprising a second layer of elastomer disposed on the layer of intumescent material.

48. A method of installing an expansion joint system, the method comprising:

compressing the expansion joint system comprising:

foam; and

a fire retardant material dispersed within the foam by infusing the fire retardant material in the foam, the foam with the fire retardant material therein configured to have a compressed density effective to pass testing as provided by UL 2079;

inserting the compressed expansion joint system into a gap between a first substrate and a second substrate; and

allowing the compressed expansion joint system to decompress to fill the gap between the first substrate and the second substrate;

wherein the expansion joint system is configured to facilitate compression of the system between the first substrate and the second substrate by repeatedly expanding and contracting to accommodate movement of the first substrate and second substrate; and

wherein the foam with the fire retardant material therein is configured to withstand exposure to a temperature of about 540° C. at about five minutes.

49. The method of claim 48 , wherein the foam has a compressed density in a range of about 200 kg/m 3 to about 700 kg/m 3 .

50. The method of claim 48 , wherein the foam has a compressed density in a range of about 400 kg/m 3 to about 450 kg/m 3 .

51. The method of claim 48 , wherein the foam with the fire retardant material uncompressed has a density of about 130 kg/m 3 to about 150 kg/m 3 .

52. The method of claim 48 , wherein the expansion joint system further comprises a water resistant layer on the foam.

53. The method of claim 48 , wherein the expansion joint system further comprises:

a first layer of an intumescent material disposed on a first surface of the foam; and

a first layer of an elastomer disposed on at least one of a second surface of the foam and the first layer of the intumescent material.