Conductive inks and method of manufacture
An ink mixture is manufactured by mixing carbon, graphite, and solvents in a mixing system which may include a Cowles disperser. The conductive portions (e.g. carbon, graphite) are evenly and universally dispersed, because an even dispersal means the conductivity of the resulting conductive strip (electrode) will be even, consistent, and reliable. The various embodiments of the ink mixture comprise a blend of different conductive pigments, including but not limited to carbon black and graphite. These embodiments must be grinded until below 6.5 Microns in particle size.
1. A method of manufacturing conductive inks, comprising:
combining a combination of carbon and graphite pigments, and solvent at a predetermined ratio;
mixing the combination using a pre-mixer;
monitoring the rate at which the pigments are combined with the solvent, to avoid overloading the pre-mixer;
forcing the mixed combination through a media grinding mill;
recirculating the mixed combination repeatedly through the media grinding mill and the pre-mixer; drying the mixed combination for one of a plurality of predetermined drying periods; and
aggregating and packaging a completed mixture in a container suitable for shipping to a printer.
2. The method of claim 1 , further comprising:
performing the manufacturing steps at a first location, and performing one or more printing steps at a second location.
3. The method of claim 1 , further comprising:
the printer being flexographic.
4. The method of claim 3 , further comprising:
manufacturing the conductive inks to be alcohol-based.
5. The method of claim 4 , further comprising:
forming the solvent to be an alcohol-based solution.
6. The method of claim 1 , further comprising:
manufacturing the conductive inks to be water-based.
7. The method of claim 1 , further comprising:
selecting the carbon and graphite pigments for inclusion in the combination based on their conductivity;
mixing the carbon pigments, graphite pigments, and the solvent in a mixing system using the pre-mixer; thereby
dispersing the carbon and graphite pigments.
8. The method of claim 1 , further comprising:
grinding the carbon and graphite pigments to be below a predetermined size limit;
measuring the size of the pigments;
if the pigments are below a predetermined size limit, stopping the grinding; and
if the pigments are not below the predetermined size limit, continuing the grinding.
9. The method of claim 8 , further comprising:
the predetermined size limit being 6.5 Microns or below.
10. The method of claim 8 , further comprising:
the pre-mixer containing a sawtooth blade.
11. The method of claim 1 , further comprising:
the solvent comprising a combination of Normal propyl alcohol and Normal propyl acetate at an 80%-20% proportion.
12. The method of claim 8 , further comprising:
configuring the pre-mixer to ensure a vortex occurs below the sawtooth blade.
13. The method of claim 8 , further comprising:
loading the media grinding mill with grinding media of a predetermined shape, size, and consistency.
14. The method of claim 13 , further comprising:
the grinding media comprising any one of steel beads, glass beads, synthetic bead, or a non-bead shape.
15. The method of claim 13 , further comprising:
the predetermined grinding media size comprising approximately ten times the predetermined size limit of the pigments being grinded.
16. The method of claim 1 , further comprising:
the media grinding mill being a horizontal media grinding mill.