Chlorine-containing resin composition
The present invention provides a chlorine-containing resin composition capable of providing a processed product that is excellent in thermal stability and heat resistance and that has various excellent properties derived from the chlorine-containing resin in an efficient, easy, simple, and high-yield manner, without degrading the appearance of the processed product. The present invention also provides a method for providing such a processed product. The present invention relates to a chlorine-containing resin composition containing a chlorine-containing resin, a hydrotalcite powder, and organic acid zinc, wherein the hydrotalcite powder contains magnesium (Mg) and/or zinc (Zn), and aluminum (Al), the molar ratio of the total amount of magnesium and zinc to the amount of aluminum ((Mg+Zn)/Al) is 2.20 or less, and the hydrotalcite powder has an oil absorption of 30 ml/100 g or less.
1. A chlorine-containing resin composition comprising:
a chlorine-containing resin;
a hydrotalcite powder;
organic acid zinc;
a plasticizer; and
stearoylbenzoylmethane or zinc dehydroacetate,
wherein the resin composition does not contain dibenzoylmethane,
the hydrotalcite powder contains magnesium (Mg) and/or zinc (Zn), and aluminum (Al),
the molar ratio of the total amount of magnesium and zinc to the amount of aluminum ((Mg+Zn)/Al) is 2.20 or less, and
the hydrotalcite powder has an oil absorption of 30 ml/100 g or less.
2. A chlorine-containing resin composition comprising:
a chlorine-containing resin;
a hydrotalcite powder; and
organic acid zinc,
wherein the hydrotalcite powder contains magnesium (Mg), zinc (Zn), and aluminum (Al),
the molar ratio of the total amount of magnesium and zinc to the amount of aluminum ((Mg+Zn)/Al) is 2.20 or less, and
the hydrotalcite powder has an oil absorption of 50 ml/100 g or less.
3. The chlorine-containing resin composition according to claim 1 ,
wherein the chlorine-containing resin composition contains 0.05 to 5 parts by mass of the hydrotalcite powder and 0.01 to 2 parts by mass of the organic acid zinc, relative to 100 parts by mass of the chlorine-containing resin.
4. The chlorine-containing resin composition according to claim 1 , wherein the hydrotalcite powder is represented by the following formula (1):
{(Mg) x (Zn) y }(Al) z (OH) 2 (A n− ) z/n .m H 2 O (1)
wherein A n− represents an n-valent interlayer anion; x, y, and z are numbers that satisfy 0<x<1, 0≤y<1, 0.2≤z≤0.4, and x+y+z=1; the ratio of x+y to z, i.e., (x+y)/z, is 2.20 or less;
and n and m are numbers that satisfy 1≤n≤4 and 0≤m, respectively.
5. A method for producing a processed product, comprising:
a step of extruding the chlorine-containing resin composition according to claim 1 by an extruder.