Polymer modified asphalt roofing material
A shingle coating asphalt composition is provided that is produced from a paving grade asphalt. The asphalt composition comprises a paving-grade asphalt that has been modified with one or more polymer additives; and a secondary additive comprising one or more of a viscosity reducing agent, a wax, a salt of a fatty acid ester, and an amide of a fatty acid. The shingle coating asphalt coating composition is used to make a shingle. The shingle includes a substrate, the asphalt, and roofing granules.
1. A roofing shingle comprising:
a substrate;
a polymer and wax modified asphalt coating on the substrate;
wherein the polymer and wax modified asphalt coating comprises:
62 wt.% to 80 wt.% of a filler based on the total weight of the polymer and wax modified asphalt coating;
an asphalt having a softening point of 60° F. to 130° F.;
2.0 wt. % to 7.0 wt. % of a polymer additive based on the total weight of the non-filler portion of the polymer and wax modified asphalt coating; and
1.6 wt. % to 3.0 wt. % of a wax based on the total weight of the non-filler portion of the polymer and wax modified asphalt coating;
wherein the polymer and wax modified asphalt coating has a softening point in the range of 200° F. to 230° F.; and a penetration at 77° F. in the range of 17 dmm to 40 dmm;
a strip of nail zone reinforcement material adhered to the polymer and wax modified asphalt coating; and
roofing granules on the polymer and wax modified asphalt coating;
wherein a longitudinal adhesion of the strip of nail zone reinforcement material to the polymer and wax modified asphalt coating is at least 20% greater than a longitudinal adhesion of an otherwise identical shingle having the same strip of nail zone reinforcement material and a conventional oxidized asphalt without the wax and the polymer additive.
2. The roofing shingle of claim 1 wherein the longitudinal adhesion of the strip of nail zone reinforcement material to the polymer and wax modified asphalt coating is more than 30% greater than the longitudinal adhesion of the otherwise identical shingle.
3. The roofing shingle of claim 1 wherein the strip of nail zone reinforcement material is a woven polyester fabric.
4. The roofing shingle of claim 1 wherein the polymer additive is styrene-butadiene rubber.
5. The roofing shingle of claim 1 wherein the wax is a Fischer-Tropsch wax.
6. The roofing shingle of claim 1 wherein the polymer additive is a radial styrene-butadiene block copolymer.
7. The roofing shingle of claim 1 wherein the wax is an ethylene bis-stearamide wax.
8. A roofing shingle comprising:
a substrate;
a polymer and wax modified asphalt coating on the substrate;
wherein the polymer and wax modified asphalt coating comprises:
62 wt.% to 80 wt.% of a filler based on the total weight of the polymer and wax modified asphalt coating;
an asphalt having a softening point of 60° F. to 130° F.;
2.0 wt. % to 7.0 wt. % of a polymer additive based on the total weight of the non-filler portion of the polymer and wax modified asphalt coating;
1.6 wt. % to 3.0 wt. % of a wax based on the total weight of the non-filler portion of the polymer and wax modified asphalt coating;
wherein the polymer and wax modified asphalt coating has a softening point in the range of 200° F. to 230° F.; and a penetration at 77° F. in the range of 17 dmm to 40 dmm;
a strip of nail zone reinforcement material adhered to the polymer and wax modified asphalt coating; and
roofing granules on the polymer and wax modified asphalt coating;
wherein a longitudinal adhesion of the strip of nail zone reinforcement material to the polymer and wax modified asphalt coating is greater than 1.25 lbf.
9. The roofing shingle of claim 8 wherein the strip of nail zone reinforcement material is a woven polyester fabric.
10. The roofing shingle of claim 8 wherein the polymer additive is styrene-butadiene rubber.
11. The roofing shingle of claim 8 wherein the wax is a Fischer-Tropsch wax.
12. The roofing shingle of claim 8 wherein the longitudinal adhesion of the strip of nail zone reinforcement material to the polymer and wax modified asphalt coating is more than 10% greater than the longitudinal adhesion of an otherwise identical shingle having the same strip of nail zone reinforcement material and an oxidized asphalt without the wax and polymer additive.
13. The roofing shingle of claim 8 wherein the polymer additive is a radial styrene-butadiene block copolymer.
14. The roofing shingle of claim 8 wherein the wax is an ethylene bis-stearamide wax.