Polycarbonate resin, and polycarbonate resin composition
Provided is a polycarbonate resin, including, as a raw material, a bisphenol A having 100 ppm by mass or less of isopropenylphenol and 250 ppm by mass or less of 2-(2-hydroxyphenyl)-2-(4-hydroxyphenyl)propane, each detected after heating in air at 175° C. for 1 hour.
1. A process for producing a polycarbonate resin, comprising: screening a bisphenol A having 100 ppm by mass or less of isopropenylphenol concentration and 250 ppm by mass or less of 2-(2-hydroxyphenyl)-2-(4-hydroxyphenyl)propane concentration, each detected after heating in air at 175° C. for 1 hour, and
producing a polycarbonate resin by subjecting the screened bisphenol A and a carbonate precursor to a reaction by an interfacial polymerization method in the presence of an aqueous solution of an alkali compound and a water-insoluble organic solvent.
2. The process for producing a polycarbonate resin according to claim 1 , wherein the bisphenol A serving as the raw material satisfies the following formula (i)
(Concentration of isopropenylphenol detected after heating at 175° C. for 1 hour)−(concentration of isopropenylphenol before heating at 175° C. for 1 hour)≤50 ppm by mass Formula (i).
3. The process for producing a polycarbonate resin according to claim 1 , wherein the polycarbonate resin has a viscosity-average molecular weight of from 9,000 to 17,500.
4. The process for producing a polycarbonate resin according to claim 1 , wherein the isopropenylphenol concentration is 50 ppm by mass or less.
5. The process for producing a polycarbonate resin according to claim 1 , wherein the 2-(2-hydroxyphenyl)-2-(4-hydroxyphenyl)propane concentration is 210 ppm by mass or less.
6. The process for producing a polycarbonate resin according to claim 1 , wherein a difference between the concentration of isopropenylphenol detected after the heating of bisphenol A in air at 175° C. for 1 hour and the concentration thereof before the heating (initial value before the heating at 175° C. for 1 hour) is 40 ppm by mass or less.
7. The process for producing a polycarbonate resin according to claim 1 , wherein the water-insoluble organic solvent comprises methylene chloride.
8. The process for producing a polycarbonate resin according to claim 1 , wherein the content of methylene chloride in the polycarbonate resin is 200 ppm by mass or less.
9. A process for producing a polycarbonate resin composition, comprising producing a polycarbonate resin according to the process of claim 1 , and blending 100 parts by mass of (A) a polycarbonate resin containing 60 mass % or more of the obtained polycarbonate resin, and 100 ppm by mass to 1,500 ppm by mass of (B) a phosphorus-based antioxidant.
10. The process for producing a polycarbonate resin composition according to claim 9 , wherein (B) the phosphorus-based antioxidant has a pentaerythritol structure.
11. The process for producing a polycarbonate resin composition according to claim 9 , wherein (B) the phosphorus-based antioxidant comprises bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritol diphosphite and/or bis(2,4-dicumylphenyl)pentaerythritol diphosphite.
12. The process for producing a polycarbonate resin composition according to claim 9 , wherein a ratio of the polycarbonate resin that is obtained by the process for producing a polycarbonate resin according to claim 1 is 80 mass % or more.
13. The process for producing a polycarbonate resin composition according to claim 9 , wherein comprising a step of blending 300 ppm by mass to 1,200 ppm by mass of (B) the phosphorus-based antioxidant based on 100 parts by mass of (A) the polycarbonate resin.
14. The process for producing a polycarbonate resin composition according to claim 9 , further comprising blending, with respect to 100 parts by mass of (A) the polycarbonate resin, 200 ppm by mass to 1,500 ppm by mass of (C) a polyorganosiloxane having a functional group.
15. The process for producing a polycarbonate resin composition according to claim 14 , wherein the functional group comprises at least one selected from the group consisting of an alkoxy group, an aryloxy group, a polyoxyalkylene group, a carboxyl group, a silanol group, an amino group, a mercapto group, an epoxy group, and a vinyl group.
16. The process for producing a polycarbonate resin composition according to claim 14 , wherein a difference between a refractive index of (C) the polyorganosiloxane and a refractive index of (A) the polycarbonate resin is 0.13 or less.
17. The process for producing a polycarbonate resin composition according to claim 14 , wherein the viscosity of (C) the polyorganosiloxane at 25° C. is 10 mm 2 /sec or more and 200 mm 2 /sec or less.
18. A process for producing a molded body, comprising:
producing a polycarbonate resin composition by the process of claim 9 , and molding the polycarbonate resin composition.
19. The molded body according to claim 18 , wherein the molded body comprises a light-guiding plate.
20. The process for producing a molded body according to claim 18 , wherein the molded body is a light-guiding member.