Carbon-coated silicon particles for lithium ion batteries
The invention relates to non-aggregated carbon-coated silicon particles having average particle diameters d 50 of 1 to 15 μm, which particles contain ≤10 wt % carbon and ≥90 wt % silicon, each based on the total weight of the carbon-coated silicon particles
1. Nonaggregated carbon-coated silicon particles for lithium batteries, comprising:
the nonaggregated carbon-coated silicon particles having average particle diameters d 50 of 1 to 15 μm, containing ≤10% by weight of carbon and ≥90% by weight of silicon, based in each case on the total weight of the carbon-coated silicon particles, wherein the nonaggregated carbon-coated silicon particles have a degree of aggregation of ≤40%,
wherein the degree of aggregation is the percentage of particles, after ultrasonic dispersion in ethanol, which are retained on a sieve having a mesh size of twice a volume-weighted D 90 value of the particles.
2. The nonaggregated carbon-coated silicon particles as claimed in claim 1 , wherein the nonaggregated carbon-coated silicon particles have a degree of aggregation of ≤30% (determined by means of sieve analysis).
3. The nonaggregated carbon-coated silicon particles as claimed in claim 1 , wherein the carbon coating of the nonaggregated carbon-coated silicon particles has an average layer thickness in the range from 1 to 100 nm as determined by: scanning electron microscopy (SEM).
4. A method for producing carbon-coated silicon particles for lithium ion batteries, comprising:
a) drying mixtures comprising silicon particles and one or more meltable carbon precursors by heating the mixtures to a temperature of <400° C. until the meltable carbon precursors have completely melted, and then the molten carbon precursors thus obtained are carbonized; or
b) coating the silicon particles with carbon by chemical vapor deposition from one or more carbon precursors, wherein the silicon particles are agitated during the chemical vapor deposition, and the chemical vapor deposition is conducted in an atmosphere containing carbon precursors to an extent of 0.1% to 80% by volume, based on the total volume of the atmosphere.
5. The method for producing the carbon-coated silicon particles as claimed in claim 4 , wherein the silicon particles used as reactant for production of nonaggregated carbon-coated silicon particles have a volume-weighted particle size distribution having diameter percentiles d 50 of 1 to less than 15 μm.
6. The method for producing the carbon-coated silicon particles as claimed in claim 5 , wherein the difference between the volume-weighted particle size distribution d 50 of the nonaggregated carbon-coated silicon particles and the volume-weighted particle size distribution d 50 of the silicon particles used as reactant for production of the nonaggregated carbon-coated silicon particles is ≤5 μm.
7. The method for producing the carbon-coated silicon particles as claimed in claim 4 , wherein one or more carbon precursors are selected from the group consisting of methane, ethane, propane, butane, pentane, isobutane, hexane, ethylene, propylene, butene, acetylene, benzene, toluene, styrene, ethylbenzene, diphenylmethane, naphthalene, phenol, cresol, nitrobenzene, chlorobenzene, pyridine, anthracene and phenanthrene.
8. The method for producing the carbon-coated silicon particles as claimed in claim 4 , wherein the chemical vapor deposition is conducted in an atmosphere containing carbon precursors to an extent of 1% to 30% by volume, based on the total volume of the atmosphere.
9. The method for producing the carbon-coated silicon particles as claimed in claim 4 , wherein one or more meltable carbon precursors are selected from the group consisting of polyacrylonitrile, mono-, di- and polysaccharides, polyaniline, polystyrene, pitches and tars.
10. An anode materials for lithium ion batteries comprising:
one or more binders,
optionally graphite,
optionally one or more further electrically conductive components and optionally one or more additives, wherein one or more carbon-coated silicon particles as claimed in claim 1 are present.
11. Lithium ion batteries comprising:
a cathode,
an anode,
a separator and an electrolyte, wherein the anode is based on an anode material as claimed in claim 10 .
12. Lithium ion batteries as claimed in claim 11 , wherein the anode material of a fully charged lithium ion battery has only been partly lithiated.
13. Lithium ion batteries as claimed in claim 12 , wherein the ratio of lithium atoms to silicon atoms in the partly lithiated anode material of the fully charged battery is ≤2.2.
14. Lithium ion batteries as claimed in claim 12 , wherein the capacity of the silicon in the anode material of the lithium ion battery is utilized to an extent of ≤50%, based on the maximum capacity of 4200 mAh per gram of silicon.