Antimicrobial articles with silver-containing alkali silicate coating and methods of making thereof
An antimicrobial article having a substrate, and a coating on a surface of the substrate. The coating includes a silver-containing alkali silicate. The antimicrobial article has an antimicrobial efficacy of greater than or equal to about 90.0% according to EPA Test Method for Efficacy of Copper Alloy Surfaces as a Sanitizer. The coating may further include at least one of a boron-containing compound and an aluminum-containing compound. A method for forming antimicrobial articles includes coating a substrate with a mixture comprising an alkali silicate; curing the coating at a temperature from greater than or equal to about 300° C. to less than or equal to about 620° C. for a duration of greater than or equal to about 15 minutes to less than or equal to about 120 minutes; and contacting the coating with an antimicrobial medium comprising silver nitrate and an alkali nitrate.
1. A method for producing an antimicrobial article, the method comprising:
coating a substrate with a mixture comprising an alkali silicate;
curing the coating at a temperature from greater than or equal to about 300° C. to less than or equal to about 620° C. for a duration of greater than or equal to about 15 minutes to less than or equal to about 120 minutes; and
contacting the coating with an antimicrobial medium comprising silver nitrate.
2. The method according to claim 1 , wherein the antimicrobial medium has a temperature from greater than or equal to about 50° C. to less than or equal to about 490° C., and the coating is contacted with the antimicrobial medium for a duration greater than or equal to about 1.0 minute to less than or equal to about 360 minutes.
3. The method according to claim 1 , wherein the antimicrobial medium is selected from the group consisting of an aqueous solution comprising saturated silver nitrate and a molten salt bath comprising silver nitrate and an alkali nitrate.
4. The method according to claim 1 , wherein the substrate is strengthened prior to coating with the mixture comprising alkali silicate, and the curing is conducted at a temperature of less than or equal to 350° C. for a duration of less than or equal to 60 minutes.
5. The method according to claim 1 , further comprising strengthening the substrate after it has been contacted with the antimicrobial medium by contacting the substrate with a strengthening medium comprising at least one alkali nitrate.
6. The method according to claim 1 , wherein the mixture comprising an alkali silicate further comprises at least one of a boron-containing compound and an aluminum-containing compound.