Curved laminated glass and manufacturing method for curved laminated glass
The present disclosure provides a curved laminated glass including a curved soda lime glass and a curved thin plate glass provided on a concave surface of the curved soda lime glass, in which a thickness of the curved soda lime glass is larger than a thickness of the curved thin plate glass, and compressive stress is formed on a surface opposite to a surface of the curved thin plate glass adjacent to the curved soda lime glass.
1. A curved laminated glass for automobile comprising:
a curved soda lime glass; and
a curved thin plate glass provided on a concave surface of the curved soda lime glass,
wherein a thickness of the curved soda lime glass is larger than a thickness of the curved thin plate glass,
wherein a first surface of the curved thin plate glass is adjacent to the curved soda lime glass, and compressive bending stress is formed on a second surface of the curved thin plate, which is opposite to the first surface of the curved thin plate glass,
wherein the curved thin plate glass is non-tempered alkali-free glass including 26 wt % to 29 wt % of Al 2 O 3 , and
wherein a Vickers hardness ratio of the curved soda lime glass to the curved thin plate glass is 1:1.1 to 1:1.3.
2. The curved laminated glass for automobile of claim 1 , wherein a thickness ratio of the curved soda lime glass to the curved thin plate glass is 1:0.1 to 1:0.5.
3. The curved laminated glass for automobile of claim 1 , wherein the thickness of the curved thin plate glass is 0.3 mm to 1.0 mm.
4. The curved laminated glass for automobile of claim 1 , wherein the curved thin plate glass is laminated onto the concave surface of the curved soda lime glass by a lamination film or an adhesive.
5. The curved laminated glass for automobile of claim 1 , wherein the curved thin plate glass has a Vickers hardness of 5.5 GPa to 7 GPa.
6. A method for manufacturing a curved laminated glass for automobile, the method comprising:
preparing a curved soda lime glass;
providing a thin plate glass which is flat on a concave surface of the curved soda lime glass; and
laminating the thin plate glass onto the concave surface of the soda lime glass by elastically deforming the thin plate glass to form a curved thin plate glass,
wherein a thickness of the curved soda lime glass is larger than a thickness of the curved thin plate glass,
wherein a first surface of the curved thin plate glass is adjacent to the curved soda lime glass, and compressive bending stress is formed on a second surface of the curved thin plate, which is opposite to the first surface of the curved thin plate glass,
wherein the curved thin plate glass is non-tempered alkali-free glass including 26 wt % to 29 wt % of Al 2 O 3 , and
wherein a Vickers hardness ratio of the curved soda lime glass to the curved thin plate glass is 1:1.1 to 1:1.3.
7. The method of claim 6 , wherein in the step of laminating, the thin plate glass is elastically deformed at a temperature of 20° C. to 35° C.
8. The method of claim 6 , wherein in the step of laminating, the curved thin plate glass is laminated onto a concave surface of the curved soda lime glass by using a lamination film or an adhesive.
9. The method of claim 6 , wherein a thickness ratio of the curved soda lime glass to the curved thin plate glass is 1:0.1 to 1:0.5.
10. The method of claim 6 , wherein the thickness of the curved thin plate glass is 0.3 mm to 1.0 mm.
11. The method of claim 6 , wherein the curved thin plate glass has a Vickers hardness of 5.5 GPa to 7 GPa.