Flame- retardant electrical cable
A flame-retardant electric cable has a core including at least one electric conductor, an electrically insulating coating and an outermost layer made from a substantially thermoplastic, low smoke zero halogen flame-retardant polymer composition. The composition includes a polymeric base made of at least one polyethylene homopolymer or copolymer having a density of 0.94 g/cm 3 at most. The composition further includes 60-64% by weight of a metal hydroxide, at least 2% by weight of an ammonium coated montmorillonite having average particle dimensions of from 5 to 20 μm, and a polysiloxane.
1. A flame-retardant electric cable having a core comprising at least one electric conductor, an electrically insulating coating, and an outermost layer made from a thermoplastic, low smoke zero halogen flame-retardant polymer composition, wherein the substantially thermoplastic low smoke zero halogen flame-retardant polymer composition comprises:
a) a polymeric base made of at least one polyethylene homopolymer or copolymer having a density of 0.94 g/cm 3 at most;
b) 60-64% by weight of a metal hydroxide;
c) at least 2% by weight of an ammonium coated montmorillonite having average particle dimensions of from 5 to 20 μm; and
d) a polysiloxane.
2. The flame-retardant electric cable according to claim 1 , wherein the outermost layer is a jacket.
3. The flame-retardant electric cable according to claim 1 , wherein the outermost layer is a skin layer.
4. The flame-retardant electric cable according to claim 3 , wherein the skin layer has a thickness of from 0.05 to 0.5 mm.
5. The flame-retardant electric cable according to claim 1 , wherein the polymeric base is made of at least one polyethylene copolymer.
6. The flame-retardant electric cable according to claim 5 , wherein at least one polyethylene copolymer is a metallocene linear low density polyethylene.
7. The flame-retardant electric cable according to claim 1 , wherein the polyethylene homopolymer or copolymer have a density in the range of 0.86 to 0.92 g/cm 3 .
8. The flame-retardant electric cable according to claim 1 , wherein the metal hydroxide is magnesium hydroxide.
9. The flame-retardant electric cable according to claim 1 , wherein the amount of montmorillonite is comprised in the range from 2 to 8% by weight.
10. The flame-retardant electric cable according to claim 1 , wherein the ammonium coated montmorillonite contains dimethyl, di(hydrogenated tallow) ammonium.
11. The flame-retardant electric cable according to claim 1 , wherein the polysiloxane is comprised in the range from 1 to 2% by weight.
12. The flame-retardant electric cable according to claim 1 , wherein the polysiloxane is polydimethylsiloxane.