Tungsten silicide target and method of manufacturing same
A tungsten silicide target capable of suppressing the occurrence of particles during sputtering is provided by a method different from conventional methods. The tungsten silicide target includes not more than 5 low-density semi-sintered portions having a size of 50 μm or more per 80000 mm 2 on the sputtering surface.
1. A tungsten silicide target comprising not more than 5 low-density semi-sintered portions having a size of 50 μm or more per 80000 mm 2 on a sputtering surface, the tungsten silicide target having an oxygen concentration of 500 ppm by mass to 2000 ppm by mass and having a maximum grain size of 20 μm or less of Si grains on the sputtering surface observed.
2. The tungsten silicide target according to claim 1 , having a Si content in excess of a stoichiometric composition WSi 2 .
3. The tungsten silicide target according to claim 1 , having a maximum grain size of 15 μm or less of Si grains on the sputtering surface observed.
4. A method of manufacturing the tungsten silicide target according to claim 1 comprising:
obtaining a mixture of a WSi 2 powder having an oxygen concentration of 500 ppm by mass to 2000 ppm by mass and a maximum grain size of 20 μm or less and a Si powder having an oxygen concentration of 500 ppm by mass to 2000 ppm by mass and a maximum grain size of 20 μm or less; and
sintering the mixture under pressure to obtain a sintered product.
5. A method of manufacturing a tungsten silicide film, comprising sputtering using the tungsten silicide target according to claim 1 .