Lubricating oil composition
The present invention provides a lubricating oil composition not containing ZnDTP but comprising: (a) a base oil; (b) molybdenum dialkyldithiocarbamate; and (c) an organic acid metal salt compound having a metal of Group 8 of a short periodic table, copper, or bismuth as a central metal.
1. A lubricating oil composition not containing ZnDTP but comprising the following components (a) to (c):
(a) a base oil;
(b) molybdenum dialkyldithiocarbamate; and
(c) an organic acid metal salt compound which is nickel 2-ethylhexanoate,
wherein a content of the molybdenum dialkyldithiocarbamate in the composition is 0.1 to 0.5 mass %, and
a content of the organic acid metal salt compound in the composition is 200 to 500 ppm in terms of nickel concentration, and
wherein the lubricating oil composition is free of an amine-based antioxidant.
2. The lubricating oil composition according to claim 1 , wherein the base oil is synthetic oil.
3. The lubricating oil composition according to claim 1 , wherein the base oil is poly alpha olefin.
4. The lubricating oil composition according to claim 1 , wherein a content of the base oil is 40 mass % or more.
5. A grease composition comprising the lubricating oil composition according to claim 1 , and a thickener.
6. The lubricating oil composition according to claim 1 , wherein the content of the molybdenum dialkyldithiocarbamate is 0.4 mass %.
7. The lubricating oil composition according to claim 1 , wherein the lubricating oil composition has a coefficient of friction measured using a ball-on-disk tester under following conditions of 0.060 or less,
Friction material: steel (SUJ-2)/steel (SUJ-2, φ 8 mm ball/disk,
Temperature: 60° C.,
Load: 10 N,
Speed: 0.5 m/s, and
Time: 30 min.
8. A lubricating oil composition not containing ZnDTP but comprising the following components (a) to (c):
(a) a base oil;
(b) molybdenum dialkyldithiocarbamate; and
(c) an organic acid metal salt compound which is cobalt 2-ethylhexanoate,
wherein a content of the organic acid metal salt compound in the composition is 100 to 1000 ppm in terms of cobalt concentration, and
wherein the lubricating oil composition is free of an anime-based antioxidant.
9. The lubricating oil composition according to claim 8 , wherein the lubricating oil composition has a coefficient of friction measured using a ball-on-disk tester under the following conditions of 0.060 or less;
Friction material: steel (SUJ-2)/steel (SUJ-2, φ 8 mm ball/disk,
Temperature: 60° C.,
Load: 10 N,
Speed: 0.5 m/s, and
Time: 30 min.
10. The lubricating oil composition according to claim 8 , wherein the base oil is synthetic oil.
11. The lubricating oil composition according to claim 8 , wherein the base oil is poly alpha olefin.
12. The lubricating oil composition according to claim 8 , wherein a content of the base oil is 40 mass % or more.
13. The lubricating oil composition according to claim 8 , wherein a content of the molybdenum dialkyldithiocarbamate in the composition is 0.1 to 10 mass % or more.
14. The lubricating oil composition according to claim 8 , wherein a content of the molybdenum dialkyldithiocarbamate in the composition is 0.1 to 0.5 mass %.
15. The lubricating oil composition according to claim 8 , wherein the content of the organic acid metal salt compound in the composition is 100 to 500 ppm in terms of cobalt concentration.
16. The lubricating oil composition according to claim 8 , wherein the content of the organic acid metal salt compound in the composition is 200 to 500 ppm in terms of cobalt concentration.
17. A grease composition comprising a lubricating oil composition not containing ZnDTP but comprising the follow components (a) to (c);
(a) a base oil;
(b) molybdenum dialkyldithiocarbamate; and
(c) an organic acid metal salt compound which is cobalt 2-ethylhexanoate,
wherein a content of the organic acid metal salt compound in the composition is 100 to 1000 ppm in terms of cobalt concentration, and
a thickener.