Selective atomic layer deposition of ruthenium
Methods of selectively depositing ruthenium are described. The preferred deposition surface changes based on the substrate temperature during processing. At high temperatures, ruthenium is deposited on a first surface of a conductive material over a second surface of an insulating material. At lower temperatures, ruthenium is deposited on an insulating surface over a conducting surface.
1. A selective deposition method comprising:
exposing a substrate comprising a conductive material having a first surface and an insulating material having a second surface to a ruthenium precursor; and
exposing the substrate to a reactant comprising one or more of O 2 , H 2 or H 2 O, wherein the substrate is maintained at a predetermined temperature, when the predetermined temperature is greater than or equal to about 250° C. ruthenium selectively deposits on the first surface over the second surface, when the predetermined temperature is less than or equal to about 200° C. ruthenium selectively deposits on the second surface over the first surface, and ruthenium is deposited with a selectivity greater than or equal to 5:1.
2. The method of claim 1 , wherein the conductive material comprises a metal, a metal nitride, a metal oxide or a combination thereof.
3. The method of claim 2 , wherein the conductive material comprises one or more of Cu, Co, W, Ta, Ti or oxides, nitrides or oxynitrides thereof.
4. The method of claim 1 , wherein the insulating material comprises silicon.
5. The method of claim 4 , wherein the insulating material comprises one or more of SiO 2 , SiN or high resistance Si.
6. The method of claim 1 , wherein the conductive material consists essentially of W and the insulating material consists essentially of SiO 2 .
7. The method of claim 1 , wherein the conductive material consists essentially of TiN and the insulating material consists essentially of SiN.
8. The method of claim 1 , wherein the ruthenium precursor comprises at least one cyclopentadienyl ligand or a derivative thereof.
9. The method of claim 8 , wherein the ruthenium precursor consists essentially of Ru(Cp) 2 or Ru(EtCp) 2 .
10. The method of claim 1 , wherein ruthenium selectively deposits on the second surface over the first surface and the substrate is maintained at a temperature in a range of about 25° C. to about 200° C.
11. The method of claim 1 , wherein ruthenium selectively deposits on the first surface over the second surface and the substrate is maintained at a temperature in a range of about 250° C. to about 500° C.
12. A selective deposition method comprising:
exposing a substrate comprising a conductive material having a first surface and an insulating material having a second surface to a ruthenium precursor; and
exposing the substrate to a reactant comprising one or more of O 2 , H 2 or H 2 O, wherein the substrate is maintained at a temperature less than or equal to about 200° C. and ruthenium selectively deposits on the second surface over the first surface with a selectivity greater than or equal to 5:1.
13. The method of claim 12 , wherein the conductive material comprises one or more of Cu, Co, W, Ta, Ti or oxides or nitrides thereof.
14. The method of claim 12 , wherein the insulating material comprises one or more of SiO 2 , SiN or high resistance Si.
15. The method of claim 12 , wherein the conductive material consists essentially of W and the insulating material consists essentially of SiO 2 .
16. The method of claim 12 , wherein the conductive material consists essentially of TiN and the insulating material consists essentially of SiN.
17. The method of claim 12 , wherein the ruthenium precursor comprises at least one cyclopentadienyl ligand or a derivative thereof.
18. The method of claim 17 , wherein the ruthenium precursor consists essentially of Ru(Cp) 2 or Ru(EtCp) 2 .