Pretreatment for application onto finished cotton fabric
Disclosed is a process for printing on cotton fabric comprising (1) contacting cotton fabric with an aqueous solution comprising (A) 40% to 70% by weight of at least one multivalent cationic salt; (B) optionally 0.1% to 5% by weight of a blocked isocyanate crosslinking agent, and (C) 3% to 40% by weight of a waterborne resin, all percentages based on the weight of the aqueous solution; (2) drying the cotton fabric to remove the water from the cotton fabric; and (3) digitally printing the pretreated and coated cotton fabric with a water-based textile ink.
1. An aqueous solution for the pretreatment of cotton fabrics consisting essentially of A) 40% to 70% by weight of at least one multivalent cationic salt; (B) 0.1% to 5% by weight of a blocked isocyanate crosslinking agent, wherein the isocyanate group in the blocked isocyanate crosslinking agent is a trifunctional trimethylolpropane (TMP) of toluene diisocyanate (TDI); hexamethylene diisocyanate (HDI), hydrogenated xylylene diisocyanate (H 6 XDI), isophorone diisocyanate (IPDI), or dicyclohexylmethane diisocyanate (H 12 NDI), or a combination thereof, and (C) 3% to 40% by weight of a waterborne resin, all percentages based on the weight of the aqueous solution.
2. The aqueous solution of claim 1 , wherein the at least one multivalent cationic salt has a cation that comprises a multivalent cation of element Mg, Ca, Sr, Ba, Sc, Y, La, Ti, Zr, V, Cr, Mn, Fe, Ru, Co, Rh, Ni, Pd, Pt, Cu, Au, Zn, Al, Ga, In, Sb, Bi, Ge, Sn and Pb, or a combination thereof.
3. The aqueous solution of claim 2 , wherein the cation is calcium.
4. The aqueous solution of claim 3 wherein the at least one multivalent cationic salt comprises from the group consisting of calcium nitrate, calcium nitrate hydrate, calcium nitrate tetrahydrate, calcium chloride, or a combination thereof.
5. The aqueous solution of claim 1 , wherein the amount of the at least one multivalent cationic salt is 47% to 62% by weight, based on the weight of the aqueous solution.
6. The aqueous solution of claim 1 , wherein the amount of the blocked isocyanate crosslinking agent is from 1% to 4% by weight, based on the weight of the aqueous solution.
7. The aqueous solution of claim 1 , wherein the waterborne resin is an acrylic resin or emulsion, a polyurethane resin or emulsion, an acrylic-vinylidene chloride copolymers, a styrene butadiene rubber latex, an acrylic styrene emulsion, a vinyl acrylic emulsion, a vinyl acetate ethylene (VAE) copolymer emulsion or a combination thereof.
8. The aqueous solution of claim 7 , wherein the amount of the waterborne resin is 4% to 25% by weight, based on the weight of the aqueous solution.
9. A process for printing on cotton fabric consisting essentially of (1) contacting the cotton fabric with an aqueous sodium hydroxide solution or an aqueous sodium carbonate solution; (2) drying the fabric; (3) rinsing the fabric with water; (4) drying the fabric: (5) contacting cotton fabric with an aqueous solution comprising (A) 40% to 70% by weight of at least one multivalent cationic salt; (B) 0.1% to 5% by weight of a blocked isocyanate crosslinking agent, wherein the isocyanate group in the blocked isocyanate crosslinking agent is a trifunctional trimethylolpropane (TMP) of toluene diisocyanate (TDI); hexamethylene diisocyanate (HDI), hydrogenated xylylene diisocyanate (H 6 XDI), isophorone diisocyanate (IPDI), or dicyclohexylmethane diisocyanate (HINDI), or a combination thereof; and (C) 3% to 40% by weight of a waterborne resin, all percentages based on the weight of the aqueous solution; (6) drying the cotton fabric to remove the water from the cotton fabric; and (7) digitally printing the pretreated and coated cotton fabric with a water-based textile ink.
10. A process for printing on cotton fabric consisting essentially of (1) contacting cotton fabric with an aqueous solution comprising (A) 40% to 70% by weight of at least one multivalent cationic salt; (B) 0.1% to 5% by weight of a blocked isocyanate crosslinking agent, wherein the isocyanate group in the blocked isocyanate crosslinking agent is a trifunctional trimethylolpropane (TMP) of toluene diisocyanate (TDI); hexamethylene diisocyanate (HDI), hydrogenated xylylene diisocyanate (H 6 XDI), isophorone diisocyanate (IPDI), or dicyclohexylmethane diisocyanate (HINDI), or a combination thereof; and (C) 3% to 40% by weight of a waterborne resin, all percentages based on the weight of the aqueous solution; (2) drying the cotton fabric to remove the water from the cotton fabric; and (3) digitally printing the pretreated and coated cotton fabric with a water-based textile ink.
11. The process of claim 10 , wherein the cotton fabric is clothing.
12. The process of claim 11 , wherein the clothing is a t-shirt.
13. The process of claim 10 , wherein the at least one multivalent cationic salt has a cation that comprises a multivalent cation of element Mg, Ca, Sr, Ba, Sc, Y, La, Ti, Zr, V, Cr, Mn, Fe, Ru, Co, Rh, Ni, Pd, Pt, Cu, Au, Zn, Al, Ga, In, Sb, Bi, Ge, Sn Pb, or a combination thereof.
14. The process of claim 13 , wherein the cation is calcium.
15. The process of claim 13 , wherein the at least one multivalent cationic salt comprises from the group consisting of calcium nitrate, calcium nitrate hydrate, calcium nitrate tetrahydrate, calcium ammonium nitrate, calcium chloride, or a combination thereof.
16. The process of any of claim 13 , wherein the amount of the at least one multivalent cationic salt is 47% to 62% by weight, based on the weight of the aqueous solution.
17. The process of claim 10 , wherein the amount of the blocked isocyanate crosslinking agent is from 1% to 4% by weight, based on the weight of the aqueous solution.
18. The process of claim 10 , wherein the waterborne resin is an acrylic resin or emulsion, a polyurethane resin or emulsion, an acrylic-vinylidene chloride copolymers, a styrene butadiene rubber latex, an acrylic styrene emulsion, a vinyl acrylic emulsion, a vinyl acetate ethylene (VAE) copolymer emulsion or a combination thereof.
19. The process of claim 18 , wherein the amount of the waterborne resin is 4% to 25% by weight, based on the weight of the aqueous solution.
20. The process of claim 10 , wherein the drying step is air drying, heat pressing, or drying in a clothing dryer.
21. The process of claim 20 , wherein the drying step is drying in a clothing dryer.
22. The process of claim 21 , wherein the drying in a clothing dryer is carried out for sufficient time to remove the water from the cotton fabric.
23. The process of claim 22 , wherein a heat pressing step is carried out between the drying in a clothing dryer and the digitally printing step.
24. The process of claim 23 , wherein a heat pressing step is carried out for 5-20 seconds at 280-400 degrees F. and at 5-80 psi within one hour of printing.
25. The process of claim 10 , wherein the digitally printing step is carried out on a direct to garment printer.
26. The process of claim 25 , wherein a white under base is first printed followed by color printing with one or more colors.
27. The process of claim 10 , wherein the digitally printed cotton fabric is heat pressed for 15-60 seconds at 280-400 degrees F. and at 5-80 psi after sitting.
28. The process of claim 10 , wherein the fabric is contacted with an aqueous sodium hydroxide solution or an aqueous sodium carbonate solution before the contacting with the aqueous solution.