Strengthened glass with ultra deep depth of compression
Chemically strengthened glass articles having at least one deep compressive layer extending from a surface of the article to a depth of compression DOC of at least about 125 μm within the glass article. The compressive stress profile includes a single linear segment or portion extending from the surface to the depth of compression DOC. Alternatively, the compressive stress profile may include an additional portion extending from the surface to a relatively shallow depth and the linear portion extending from the shallow depth to the depth of compression.
1. A glass article, the glass article comprising a thickness tin a range from 0.1 mm up to 1.0 mm and a compressive region having a compressive stress CS s in a range from 400 MPa to 1200 MPa at a surface of the glass article, wherein the compressive region extends from the surface to a depth of compression DOC, wherein 0.1 t≤DOC≤0.25 t, and has a compressive stress profile, the compressive stress profile comprising:
a. a first portion b extending from the surface to a first depth below the surface and having a slope m b , wherein −40 MPa/μm≥m b ≥−200 MPa/μm, wherein the first depth is in a range from 3 μm to 15 μm; and
b. a second portion c extending from a second depth below the surface to the depth of compression DOC and having a slope m c , wherein −0.4 MPa/μm≥m c ≥−3.0 MPa/μm, wherein the second depth is in a range from 3 μm to 15 μm.
2. The glass article of claim 1 , wherein the depth of compression DOC is in a range from 95 μm to 250 μm.
3. The glass article of claim 2 , wherein the depth of compression DOC is in a range from 100 μm to 190 μm.
4. The glass article of claim 1 , wherein 0.12 t≤DOC≤0.22 t.
5. The glass article of claim 1 , wherein the slope mc is in a range from −0.7 MPa/μm to −2.7 MPa/μm.
6. The glass article of claim 5 , wherein the slope mc is in a range from −1.5 MPa/μm to −2.7 MPa/μm.
7. The glass article of claim 1 , wherein the glass article comprises an alkali aluminosilicate glass.
8. The glass article of claim 7 , wherein the alkali aluminosilicate glass comprises up to 10 mol % Li 2 O.
9. The glass article of claim 7 , wherein the alkali aluminosilicate glass comprises at least 4 mol % P 2 O 5 and from 0 mol % to 4 mol % B 2 O 3 , wherein 1.3<[(P 2 O 5 +R 2 O)/M 2 O 3 ]≤2.3, where M 2 O 3 =Al 2 O 3 +B 2 O 3 , and R 2 O is the sum of monovalent cation oxides present in the alkali aluminosilicate glass.
10. The glass article of claim 7 , wherein the glass is lithium-free.
11. The glass article of claim 7 , wherein the glass consists essentially of
from 40 mol % to 70 mol % SiO 2 ;
from 4 mol % to 15 mol % P 2 O 5 ;
from 13 to 30 mol % R x O, wherein R x O is the sum of the alkali metal oxides, alkaline earth metal oxides, and transition metal monoxides present in the glass, wherein R x O comprises from 13 mol % to 25 mol % Na 2 O and from 0 mol % to 1 mol % K 2 O,
from 11 to 29 mol % M 2 O 3 , where M 2 O 3 =Al 2 O 3 +B 2 O 3 , wherein M 2 O 3 comprises from 11 mol % to 25 mol % Al 2 O 3 , and from 0 mol % to 4 mol % B 2 O 3 ;
and 3 mol % or less of one or more of TiO 2 , MnO, Nb 2 O 5 , MoO 3 , Ta 2 O 5 , WO 3 , ZrO 2 , Y 2 O 3 , La 2 O 3 , HfO 2 , CdO, SnO 2 , Fe 2 O 3 , CeO 2 , As 2 O 3 , Sb 2 O 3 , Cl, and Br;
and 1.3<[(P 2 O 5 +R 2 O)/M 2 O 3 ]≤2.3, where R 2 O is the sum of monovalent cation oxides present in the glass.
12. An electronic device comprising the glass article of claim 1 .