Magnetic tunnel junction, spintronics device using same, and method for manufacturing magnetic tunnel junction

1. A magnetic tunnel junction, comprising:

a tunnel barrier layer provided between a first magnetic layer and a second magnetic layer,

wherein the tunnel barrier layer is a crystal body made of a stacked structure of a first insulating layer and a second insulating layer, the crystal body is oriented,

the first insulating layer is made of an oxide of Mg 1-x X x (0≤x≤0.15), wherein X is at least one element selected from the group consisting of Al and Ti,

a thickness of the first insulating layer is not less than 0.05 nm and not more than 1.2 nm,

the second insulating layer is crystalline and made of an oxide of an alloy comprising at least two elements selected from the group consisting of Mg, Al, Zn, and Li,

a sum of the thickness of the first insulating layer and a thickness of the second insulating layer is not less than 0.6 nm and not more than 3 nm, and

both the first magnetic layer and the second magnetic layer are made of an alloy comprising B and at least one element selected from the group consisting of Co and Fe.

2. The magnetic tunnel junction according to claim 1 , further comprising:

a layer comprising at least one element selected from the group consisting of Co and Fe at both or one of between the tunnel barrier layer and the first magnetic layer or between the tunnel barrier layer and the second magnetic layer.

3. The magnetic tunnel junction according to claim 1 , wherein the first insulating layer is made of MgO.

4. The magnetic tunnel junction according to claim 1 , wherein the second insulating layer is made of an oxide of Mg 1-y Al y (0.2≤y≤0.8).

5. The magnetic tunnel junction according to claim 1 , having a tunnel magneto-resistance not less than 120% and not more than 34000% at room temperature.

6. A spintronics device, comprising the magnetic tunnel junction according to claim 1 .

7. The spintronics device according to claim 6 , wherein the spintronics device is one of a hard disk magnetic head, a spin torque rewritable MRAM, a three-terminal MRAM, a voltage-driven MRAM, a spin torque oscillator, or a spin resonance tunnel element.

8. The magnetic tunnel junction according to claim 1 , wherein the first insulating layer and the second insulating layer are (001) grown orientation films.

9. A method for manufacturing a magnetic tunnel junction according to claim 1 , the method comprising:

i) introducing a substrate to a sputtering apparatus;

ii) forming a first magnetic layer at the substrate;

iii) forming a first insulating layer to overlap the first magnetic layer, a thickness of the first insulating, layer being not less than 0.05 nm and not more than 1.2 nm;

iv) forming a second insulating layer to overlap the first insulating layer, a sum of the thickness of the first insulating layer and a thickness of the second insulating layer being not less than 0.6 nm and not more than 3 nm;

v) forming a second magnetic layer to overlap the second insulating layer; and

vi) performing heat treatment of a multilayer film structure that is made,

wherein the heat treatment is performed in a vacuum for 1 minute to 60 minutes at a temperature range from 300° C. to 500° C., and

after the heat treatment, the second insulating layer is crystalline.

10. The method according to claim 9 , wherein the forming ii) is performed after forming Ta at the substrate, and the Ta is an underlayer structure film.

11. The method according to claim 9 , further comprising:

ii-a) forming a first magnetic insertion layer to overlap the first magnetic layer between the forming ii) and the forming iii).

12. The method according to claim 9 , further comprising:

iv-a) forming a second magnetic insertion layer to overlap the second insulating layer between the forming iv) and the forming v).

13. The method according to claim 9 , further comprising:

forming Ta as an upper structure film to overlap the second magnetic layer between the forming v) and the forming vi).

14. The method according t claim 9 , wherein after the heat treatment, the first insulating layer and the second insulating layer are (001) grown orientation films.