Metal gate structure and methods thereof
Provided is a metal gate structure and related methods that include performing a metal gate cut process. The metal gate cut process includes a plurality of etching steps. For example, a first anisotropic dry etch is performed, a second isotropic dry etch is performed, and a third wet etch is performed. In some embodiments, the second isotropic etch removes a residual portion of a metal gate layer including a metal containing layer. In some embodiments, the third etch removes a residual portion of a dielectric layer.
1. A method of semiconductor device fabrication, comprising:
forming a first fin and a second fin on a substrate;
forming a gate structure over the first and second fins, wherein the gate structure extends from the first fin to the second fin; and
performing a line-cut process to separate the gate structure into a first metal gate structure and a second metal gate structure with an interposing space, wherein the line-cut process includes:
performing a first anisotropic etch to remove a first portion of a plurality of metal layers of the gate structure, wherein the first anisotropic etch has a first etchant gas;
after the first anisotropic etch, performing a second isotropic etch to remove a second portion of the gate structure, the second portion including a region of at least one metal layer of the plurality of metal layers, wherein the second isotropic etch has a second etchant gas different than the first etchant gas; and
after the second isotropic etch, performing a third wet etch to remove a third portion of the gate structure, the third portion including a residual portion of a gate dielectric layer.
2. The method of claim 1 , wherein the first anisotropic etch is a dry etch and the second isotropic etch is a dry etch.
3. The method of claim 1 , wherein the first etchant gas includes C12; and wherein the second etchant gas is NF3.
4. The method of claim 1 , wherein the second isotropic etch is a selective etch to the at least one metal layer and does not substantially etch silicon oxide.
5. The method of claim 4 , further comprising: forming a shallow trench isolation (STI) feature between the first fin and the second fin, wherein the STI feature includes silicon oxide.
6. The method of claim 4 , wherein the at least one metal layer that the second isotropic etch is selective to is one of TiN, TaN, or TaSiN.
7. The method of claim 1 , wherein after performing the first anisotropic etch process and before performing the second isotropic etch, a trench is provided in the interposing space, the trench having substantially vertical sidewalls.
8. The method of claim 7 , wherein after performing the second isotropic etch and prior to performing the third wet etch, the trench has a cut region providing a first portion of the trench sidewall oblique with respect to a second portion of the trench sidewall that is substantially vertical.
9. The method of claim 1 , wherein the third wet etch includes HF etchant.
10. A method, comprising:
forming a metal gate structure in a trench over a substrate, wherein the forming the metal gate structure includes:
forming a gate dielectric layer;
forming a first metal layer over the gate dielectric layer; and
forming a second metal layer over the first metal layer; and
performing a cut gate process on the metal gate structure to form a first portion of the metal gate structure and a second portion of the metal gate structure, the first and second portions having a cut region there between, wherein the performing the cut gate process includes:
performing a first etching process to remove a first region of the second metal layer, a first region of the first metal layer and a first region of the gate dielectric layer, wherein the first etching process provides an opening between the first and second portions having substantially vertical sidewalls;
performing a second etching process to remove a second region of the first metal layer, wherein the second etching process modifies the substantially vertically sidewalls to provide an upper portion having substantially vertical sidewalls and a bottom portion having sidewalls being oblique to the substantially vertical sidewalls of the upper portion; and
performing a third etching process to remove a second region of the gate dielectric layer.
11. The method of claim 10 , wherein after the second etching process the bottom portion sidewalls are defined by the second region of the gate dielectric layer.
12. The method of claim 10 , wherein the second metal layer is completely removed from the cut region by the first etching process.
13. The method of claim 12 , wherein the first metal layer is completely removed from the cut region by a combination of the first etching process and the second etching process.
14. The method of claim 13 , wherein the gate dielectric layer is completely removed from the cut region by a combination of the first etching process, the second etching process, and the third etching process.
15. The method of claim 10 , wherein each of the first, second and third etching processes use a different etchant.
16. A method of semiconductor device fabrication, comprising:
forming a first fin and a second fin on a substrate;
forming a gate structure over the first and second fins, wherein the gate structure extends from the first fin to the second fin and includes a plurality of metal layers and a gate dielectric layer; and
separating the gate structure into a first gate structure and a second gate structure with an interposing space by:
performing a first dry etch to remove a first portion of the plurality of metal layers of the gate structure, wherein the first dry etch uses a first etchant gas;
after the first etch, performing a second dry etch to remove a second portion of at least one metal layer of the plurality of metal layers, wherein the second dry etch has a second etchant gas different than the first etchant gas; and
after the second dry etch, performing a third wet etch to remove a portion of a gate dielectric layer.
17. The method of claim 16 , wherein the first dry etch is an anisotropic etch and the second dry etch is an isotropic etch.
18. The method of claim 16 , wherein the first gate structure is disposed over the first fin and the second gate structure is disposed over the second fin.
19. The method of claim 16 , wherein after the performing the third wet etch, the interposing space is disposed above a shallow trench isolation (STI) feature extending from the first fin to the second fin, the interposing space exposing a top surface of the STI feature.
20. The method of claim 16 , wherein after performing the second dry etch and prior to performing the third wet etch, each of the plurality of metal layers are removed from the substrate.