Particle for making metal parts using 3D printing and method for making metal parts
Particle ( 1 ) which comprises a core ( 2 ) made of copper, of a copper alloy, of aluminium or of an aluminium alloy, covered with an external layer ( 3 ), where the external layer ( 3 ) is formed from metal nanoparticles or carbon nanotubes.
1. A particle comprising a core made of aluminium or of an aluminium alloy, covered successively with: a stack of one or more metallic layers, the stack comprising at least one continuous layer completely covering the core of the particle, wherein the at least one continuous layer is made of manganese and/or magnesium; and an external layer formed from metal nanoparticles or carbon nanotubes;
wherein the particle is in the form of a powder for 3D printing.
2. The particle according to claim 1 , wherein the nanoparticles are made of copper.
3. The particle according to claim 1 , wherein the nanoparticles have a diameter which ranges from 1 nm to 500 nm.
4. The particle according to claim 1 , wherein the core of the particle has a diameter which ranges from 1 μm to 150 μm.
5. The particle according to claim 1 , wherein the metallic layer or layers are each made of one metal chosen, independently, from gold, platinum, silver, manganese, magnesium, zirconium, zinc, silicon, nickel or copper.
6. The particle according to claim 1 , wherein the external layer and the layer of the stack which is in contact with the external layer are made of copper.
7. The particle according to claim 1 , wherein the at least one continuous layer further comprises copper, nickel, tin, or chromium.
8. The particle according to claim 1 , wherein the at least one continuous layer further comprises zirconium, zinc, silicon, or nickel.
9. The particle according to claim 1 , wherein the at least one continuous layer of the stack further comprises copper.
10. The particle according to claim 1 , wherein the core of the particle is made of aluminium, the core being covered by a stack comprising a layer made of manganese, a layer made of magnesium and a layer made of copper, and by an external layer of copper nanoparticles.
11. The particle according to claim 1 , wherein the external layer is formed from metal nanoparticles.
12. A method for manufacturing a metal part by 3D printing comprising at least the following successive steps:
a1) supplying a powder comprising particles as defined in claim 1 ,
b1) forming a bed of particles on a substrate,
c1) localised melting of the powder bed so as to form a first molten zone, and solidification of the first molten zone of particles so as to form a first solidified zone.
13. The method according to claim 12 , wherein the steps b1) and c1) are repeated at least once so as to form at least one other solidified zone on the first solidified zone.
14. The method according to claim 12 , wherein the core of the particles is made of aluminium, with the core being covered by a stack comprising a layer made of manganese, a layer made of magnesium and a layer made of copper, and by an external layer of copper nanoparticles, and in that the solidified layer is a 2024 aluminium alloy.
15. The method according to claim 12 , wherein the core of the particles is made of 6060 aluminium, with the core being covered by a stack comprising a layer made of magnesium and a layer made of copper, and by an external layer of copper nanoparticles, and in that the solidified layer is a 6061 aluminium alloy.
16. The method according to claim 12 , wherein the core of the particles is made of 2117 aluminium, with the core being covered by a stack comprising a layer made of manganese, a layer made of magnesium and a layer made of copper, and by an external layer of copper nanoparticles, and in that the solidified layer is a 2024 aluminium alloy.
17. The method for manufacturing a metal part by 3D printing comprising at least the following successive steps:
a2) supplying a powder comprising particles as defined in claim 1 ,
b2) projecting the powder onto a substrate, where the powder passes through a laser beam before reaching the substrate, so that it is melted,
c2) solidifying the molten powder on the substrate so as to create a first solidified zone.
18. The method according to claim 17 , wherein the steps b2) and c2) are repeated at least once so as to form at least one other solidified zone on the first solidified zone.
19. The method according to claim 17 , wherein the core of the particles is made of aluminium, with the core being covered by a stack comprising a layer made of manganese, a layer made of magnesium and a layer made of copper, and by an external layer of copper nanoparticles, and in that the solidified layer is a 2024 aluminium alloy.
20. The method according to claim 17 , wherein the core of the particles is made of 6060 aluminium, with the core being covered by a stack comprising a layer made of magnesium and a layer made of copper, and by an external layer of copper nanoparticles, and in that the solidified layer is a 6061 aluminium alloy.
21. The method according to claim 17 , wherein the core of the particles is made of 2117 aluminium, with the core being covered by a stack comprising a layer made of manganese, a layer made of magnesium and a layer made of copper, and by an external layer of copper nanoparticles, and in that the solidified layer is a 2024 aluminium alloy.