Silver-plated product and method for producing same
A silver-plated product is produced by forming a surface layer of silver on a base material by electroplating at a liquid temperature of 10 to 35° C. and a current density of 3 to 15 A/dm 2 in a silver plating solution so as to satisfy (32.6x−300)≤y≤(32.6x+200) assuming that a product of a concentration of potassium cyanide in the silver plating solution and a current density is y (g·A/L·dm 2 ) and that a liquid temperature of the silver plating solution is x (° C.), the silver plating solution containing 80 to 110 g/L of silver, 70 to 160 g/L of potassium cyanide and 55 to 70 mg/L of selenium.
1. A method for producing a silver-plated product, the method comprising the steps of:
preparing a silver plating solution which contains 80 to 110 g/L of silver, 70 to 160 g/L of potassium cyanide and 55 to 70 mg/L of selenium; and
forming a surface layer of silver on a base material by electroplating at a liquid temperature of 10 to 35° C. and a current density of 3 to 15 A/dm 2 in the silver plating solution so as to satisfy (32.6x−300)≤y≤(32.6x+200) assuming that a product of a concentration of potassium cyanide in the silver plating solution and the current density is y (g·A/L·dm 2 ) and that the liquid temperature of the silver plating solution is x (° C.).
2. A method for producing a silver-plated product as set forth in claim 1 , wherein said silver plating solution is an aqueous solution containing silver potassium cyanide, potassium cyanide and potassium selenocyanate.
3. A method for producing a silver-plated product as set forth in claim 1 , wherein said base material is made of copper or a copper alloy.
4. A method for producing a silver-plated product as set forth in claim 1 , wherein an underlying layer of nickel is formed between said base material and said surface layer.