Electrostatic adsorbable laminated sheet and display material
It is intended to provide an electrostatic adsorbable laminated sheet which is less likely to cause paste residues, etc. upon peeling from an adherend, exhibits further enhanced adsorbability to an adherend, additionally exhibits enhanced adhesiveness at an electrostatic adsorbable interface, and thereby has enhanced handleability. Electrostatic adsorbable laminated sheet includes label layer, support layer, and grip layer disposed between the label layer and the support layer, wherein the label layer and the support layer are electrostatically adsorbed to each other via the grip layer.
1. An electrostatic adsorbable laminated sheet comprising
a label layer, a support layer, and a grip layer disposed between the label layer and the support layer, wherein
the grip layer comprises a polyolefin resin selected from a polypropylene resin and a polyethylene resin,
the label layer and the support layer are electrostatically adsorbed to each other via the grip layer, and
an adhesiveness between the label layer and the support layer is 60 g/cm 2 or more.
2. The electrostatic adsorbable laminated sheet according to claim 1 , further comprising
a second grip layer disposed between the grip layer and the support layer, wherein
the grip layer and the second grip layer are electrostatically adsorbed to each other.
3. The electrostatic adsorbable laminated sheet according to claim 1 , further comprising
a second support layer placed on a surface, opposite to the surface where the support layer is placed, of the label layer, and a grip layer disposed between the label layer and the second support layer, wherein
the label layer and the second support layer are electrostatically adsorbed to each other via the grip layer disposed between the label layer and the second support layer.
4. The electrostatic adsorbable laminated sheet according to claim 1 , further comprising
a pressure-sensitive adhesive layer at the outer side of the label layer.
5. The electrostatic adsorbable laminated sheet according to claim 4 , further comprising
a protective layer as an outermost layer at the label layer side or the pressure-sensitive adhesive layer side.
6. The electrostatic adsorbable laminated sheet according to claim 1 , wherein the label layer is a layer containing a thermoplastic resin.
7. The electrostatic adsorbable laminated sheet according to claim 1 , wherein
the grip layer satisfies the following conditions (1) and/or (2):
(1) the grip layer comprises a propylene resin, wherein when maximum values of absorbance in the ranges of 920±0.5 cm −1 , 974±0.5 cm −1 , and 998±0.5 cm −1 measured on the grip layer surface by ATR infrared spectroscopy are defined as A 920 , A 974 , and A 998 , respectively, a degree of isotactic crystallinity of the grip layer determined according to the following (Expression 1) is 20 to 65%:
Degree of isotactic crystallinity (%)=109×( A 998 −A 920 )/( A 974 −A 920 )−31.4 (Expression 1); and
(2) the grip layer comprises an ethylene resin, wherein when maximum values of absorbance in the ranges of 731±1 cm −1 and 720±1 cm −1 measured on the grip layer surface by ATR infrared spectroscopy are defined as A 731 and A 720 , respectively, a degree of polyethylene crystallinity of the grip layer determined according to the following (Expression 2) is 20 to 85%:
Degree of polyethylene crystallinity (%)=100×( A 731 /A 720 ) (Expression 2),
except that in the case where the grip layer satisfies the conditions (1) and (2), the condition (1) is applied when A 720 /A 974 is less than 1.0, and the condition (2) is applied when A 720 /A 974 is 1.0 or more.
8. The electrostatic adsorbable laminated sheet according to claim 1 , wherein arithmetic mean roughness (Ra) of at least one surface of the grip layer measured according to JIS B0601: 2003 is 0.1 to 1.0 μm.
9. The electrostatic adsorbable laminated sheet according to claim 1 , wherein surface resistivity of at least one surface of the grip layer measured according to JIS C2151: 2006 is 1×10 13 to 9×10 17 Ω.
10. The electrostatic adsorbable laminated sheet according to claim 1 , wherein bending stiffness (Gurley method) of the label layer and the grip layer, or the label layer and the support layer measured according to bending repulsion method A of JIS L1096: 2010 is 0.05 to 10 mN.
11. A display material comprising
a label layer, and a grip layer in contact with the label layer, wherein
the grip layer comprises a polyolefin resin selected from a polypropylene resin and a polyethylene resin,
the display material has electrostatic adsorbability, and
the grip layer satisfies the following conditions (1) and/or (2):
(1) the grip layer comprises a propylene resin, wherein when maximum values of absorbance in the ranges of 920±0.5 cm −1 , 974±0.5 cm −1 , and 998±0.5 cm −1 measured on the grip layer surface by ATR infrared spectroscopy are defined as A 920 , A 974 , and A 998 , respectively, a degree of isotactic crystallinity of the grip layer determined according to the following (Expression 1) is 20 to 65%:
Degree of isotactic crystallinity (%)=109×( A 998 −A 920 )/( A 974 −A 920 )−31.4 (Expression 1); and
(2) the grip layer comprises an ethylene resin, wherein when maximum values of absorbance in the ranges of 731±1 cm −1 and 720±1 cm −1 measured on the grip layer surface by ATR infrared spectroscopy are defined as A 731 and A 720 , respectively, a degree of polyethylene crystallinity of the grip layer determined according to the following (Expression 2) is 20 to 85%:
Degree of polyethylene crystallinity (%)=100×( A 731 /A 720 ) (Expression 2),
except that in the case where the grip layer satisfies the conditions (1) and (2), the condition (1) is applied when A 720 /A 974 is less than 1.0, and the condition (2) is applied when A 720 /A 974 is 1.0 or more.
12. The electrostatic adsorbable laminated sheet according to claim 1 , wherein
the grip layer comprises a propylene resin having an endothermic peak at 120° C. to 180° C. and a resin having no endothermic peak at 0° C. to 200° C.