Stable ethylsilicate polymers and method of making the same
Ethylsilicate polymers and a method of making, specifically ethylsilicate polymer binders with reduced levels of regulated volatile organic compounds (VOCs) for use in the coatings industry and casting industry, and more specifically to stable, fast cure ethylsilicate polymer binders with low levels of regulated VOCs.
1. A method of forming a polyethylsilicate composition,
wherein said method comprises:
adding an ethanol, an acid and a silica source to a reactor;
heating the reactor after said adding;
adding an ethylsilicate source to the reactor to initiate a hydrolysis reaction; and
adding propylene carbonate to the reactor after the hydrolysis reaction, to obtain said polyethylsilicate composition comprising the polyethylsilicate, 18-80% by weight of SiO 2 based on a total weight of the composition, the acid, ethanol, and propylene carbonate in an amount of up to 30% by weight based on the total weight of the composition, and wherein the ethanol and propylene carbonate in combination form less than 70% by weight, based on the total weight of the composition.
2. The method of claim 1 , further comprising adding parachlorobenzotrifluoride to the reactor after the hydrolysis reaction.
3. The method of claim 1 , further comprising stripping ethanol from the reactor after the hydrolysis reaction.
4. The method of claim 1 , wherein said silica source is a colloidal silica sol.
5. The method of claim 1 , further comprising adding a propylene carbonate before said adding of the ethylsilicate source.
6. The method of claim 1 , further comprising adding a propylene carbonate during said adding of the ethylsilicate source.
7. The method of claim 1 , further comprising adding a polyethylsilicate source.
8. A method of forming a polyethylsilicate composition, said method comprising:
adding a silica source and a propylene carbonate to a reactor; and
adding an ethylsilicate source to the reactor to initiate a hydrolysis reaction, to obtain said polyethylsilicate composition comprising said polyethylsilicate, 18-50% by weight of SiO 2 based on a total weight of the composition, 0 to 60% by weight of an alcohol based on the total weight of the composition, and a positive amount of up to 40% by weight of propylene carbonate based on the total weight of the composition, and wherein the alcohol and propylene carbonate in combination comprise 5-70% by weight, based on the total weight of the composition.
9. The method of claim 8 , further comprising adding tert-butylacetate to the reactor after said hydrolysis reaction.
10. The method of claim 8 , further comprising adding additional propylene carbonate after said hydrolysis reaction.
11. The method of claim 8 , further comprising:
adding a mineral acid to the reactor before said hydrolysis reaction;
adding a solvent after said hydrolysis reaction, said solvent being selected from the group consisting of propylene carbonate, tert-butylacetate, and parachlorobenzotrifluoride; and
adding a polyethylsilicate after said hydrolysis reaction.
12. A method of forming a polyethylsilicate composition
said method comprising:
adding ethanol, an acid and a silica source, and propylene carbonate to a reactor;
heating the reactor after said adding; and
hydrolizing the contents of the reactor,
to obtain the polyethylsilicate composition comprising polyethylsilicate, 18-80% by weight of SiO 2 based on a total weight of the composition, an acid, ethanol, and propylene carbonate in an amount of up to 30% by weight based on the total weight of the composition, and wherein the ethanol and propylene carbonate in combination form less than 70% by weight, based on the total weight of the composition.
13. The method of claim 12 , wherein said hydrolizing the contents of the reactor further comprises adding water to the reactor.
14. The method of claim 12 , wherein said silica source is a polyethylsilicate.
15. The method of claim 11 , wherein said solvent is tert-butylacetate.
16. The method of claim 11 , wherein said solvent is parachlorobenzotrifluoride.
17. The method of claim 11 , wherein said solvent is tert-butylacetate and parachlorobenzotrifluoride.