Surface-coated cutting tool
To improve the adhesion resistance and wear resistance of a surface-coated cutting tool. The surface-coated cutting tool includes a tool substrate, and a single-component coating layer composed of a composite nitride of Cr (chromium), Al (aluminum), and V (vanadium) and disposed on the surface of the tool substrate. The composite nitride is characterized by being represented by a compositional formula: Cr a Al b V c N satisfying the following relations: 0.11≤ a ≤0.26; 0.73≤ b ≤0.85; 0< c ≤0.04; and a+b+c ≤1 (wherein a, b, and c each represent an atomic proportion). The single-component coating layer has both a hexagonal phase and a cubic phase.
1. A surface-coated cutting tool comprising a tool substrate, and a single-component coating layer composed of a composite nitride of Cr, Al, and V and disposed on the surface of the tool substrate, wherein
the composite nitride being represented by a compositional formula: Cr a Al b V c N satisfying the following relations:
0.11≤ a≤ 0.26;
0.73≤ b≤ 0.85;
0< c≤ 0.04; and
a+b+c= 1
(wherein a, b, and c each represent an atomic proportion),
wherein the single-component coating layer has both a hexagonal phase and a cubic phase, and
wherein the single-component coating layer exhibits a peak intensity ratio (IA/IB) of 1.5 or more and 5.8 or less as determined by X-ray diffractometry, wherein
IA represents the peak intensity of (111) plane of the cubic phase, and
IB represents the peak intensity of (100) plane of the hexagonal phase.
2. A surface-coated cutting tool according to claim 1 , wherein the single-component coating layer exhibits a peak intensity ratio (IA/IC) of 0.9 or more as determined through X-ray diffractometry, wherein
IC represents the peak intensity of (200) plane of the cubic phase.
3. A surface-coated cutting tool comprising a tool substrate, and a single-component coating layer composed of a composite nitride of Cr, Al, and V and disposed on the surface of the tool substrate, wherein
the composite nitride being represented by a compositional formula: Cr a Al b V c N satisfying the following relations:
0.11≤ a≤ 0.26;
0.73≤ b≤ 0.85;
0< c≤ 0.04; and
a+b+c= 1
(wherein a, b, and c each represent an atomic proportion),
wherein the single-component coating layer has both a hexagonal phase and a cubic phase, and
wherein the single-component coating layer exhibits a peak intensity ratio (IA/IC) of 0.9 or more as determined through X-ray diffractometry, wherein
IC represents the peak intensity of (200) plane of the cubic phase.