Porous halloysite powder and method for producing halloysite powder
Provided are a halloysite powder and a method for producing the halloysite powder. The halloysite powder contains granules in which halloysite including halloysite nanotubes is aggregated. The granules have first pores derived from the tube holes in the halloysite nanotubes and second pores that are different from the first pores.
1. A halloysite powder comprising a granule that is an aggregate of halloysite including a halloysite nanotube,
wherein the granule includes a first pore derived from a tube hole of the halloysite nanotube, and a second pore different from the first pore,
wherein a differential pore distribution determined from a nitrogen adsorption isotherm by the BJH method exhibits two or more pore size peaks of 10 nm or more, and
wherein an average particle size of the granule is from 0.5 to 200 μm.
2. The halloysite powder according to claim 1 , wherein the differential pore distribution exhibits a pore size peak in a range from 10 nm to 20 nm and a pore size peak of greater than 20 nm.
3. The halloysite powder according to claim 2 , wherein an initial bulk density is not less than 0.40 g/cm 3 .
4. The halloysite powder according to claim 2 , wherein a tap bulk density is not less than 0.70 g/cm 3 .
5. The halloysite powder according to claim 1 , wherein an initial bulk density is not less than 0.40 g/cm 3 .
6. The halloysite powder according to claim 5 , wherein a tap bulk density is not less than 0.70 g/cm 3 .
7. The halloysite powder according to claim 1 , wherein a tap bulk density is not less than 0.70 g/cm 3 .
8. The halloysite powder according to claim 1 , wherein an angle of repose is not greater than 50°.
9. The halloysite powder according to claim 1 , wherein a BET specific surface area is from 30 to 200 m 2 /g.
10. The halloysite powder according to claim 1 , wherein an average pore size is not less than 11.0 nm.
11. The halloysite powder according to claim 1 , wherein a total pore area is not less than 59.0 m 2 /g.
12. The halloysite powder according to claim 1 , wherein a total pore volume is not less than 0.20 cm 3 /g.
13. The halloysite powder according to claim 1 , wherein a quartz content is not greater than 1.00 mass %.
14. A method of producing the halloysite powder described in claim 1 , comprising:
a step of preparing a slurry of halloysite including a halloysite nanotube; and
a step of preparing powder from the slurry,
wherein the solid content concentration of the slurry is 30 mass % or less.
15. The method of producing a halloysite powder according to claim 14 , further comprising a step of firing the prepared powder.
16. The method of producing a halloysite powder according to claim 15 , wherein the step of preparing powder from the slurry is a step of spray-drying the slurry.
17. The method of producing a halloysite powder according to claim 15 , wherein the step of preparing powder from the slurry is a step of media-fluidized-drying the slurry.
18. The method of producing a halloysite powder according to claim 14 , wherein the step of preparing powder from the slurry is a step of spray-drying the slurry.
19. The method of producing a halloysite powder according to claim 14 , wherein the step of preparing powder from the slurry is a step of media-fluidized-drying the slurry.