High temperature treated media
A thermally bonded filtration media that can be used in high temperature conditions in the absence of any loss of fiber through thermal effects or mechanical impact on the fiber components is disclosed. The filter media can be manufactured and used in a filter unit or structure, can be placed in a stream of removable fluid, and can remove a particulate load from the mobile stream at an increased temperature range. The combination of bi-component fiber, other filter media fiber, and other filtration additives provides an improved filtration media having unique properties in high temperature, high performance applications.
1. A filter element comprising a filter medium comprising a media layer comprising fibers in a thermally bonded nonwoven web, the web comprising:
(a) a bi-component fiber having a structural polymer portion and a thermoplastic binder polymer portion, wherein the structural polymer portion has a melting point of at least 240 ° C. and the binder polymer portion has a melting point of up to 115 ° C.; and the bi-component fiber has a diameter of about 5 μm to 25 μm;
(b) a bi-component fiber having a structural polymer portion and a thermoplastic binder polymer portion, wherein the structural polymer portion has a melting point of at least 240 ° C. and the binder polymer portion has a melting point of 120 ° C. to 170 ° C.; and the bi-component fiber has a diameter of about 5 μm to 25 μm; and
(c) a staple fiber;
wherein the web comprises about 5 wt-% to 25 wt-%, based on the weight of the web, of the bi-component fiber of part (a);
wherein the web comprises about 25 wt-% to 60 wt-%, based on the weight of the web, of the bi-component fiber of part (b); and
wherein the web has a solidity of under 10 %.
2. The filter element of claim 1 , the web comprising about 10 wt-% to 70 wt-%, based on the weight of the web, of the staple fiber; and wherein the web has a thickness of about 0.1 mm to 2 cm.
3. The filter element of claim 1 , wherein the bi-component fibers of (a) and (b) have a length of about 2 mm to about 15 mm.
4. The filter element of claim 1 , wherein the web has a basis weight of about 45 g/m 2 to 150 g/m 2.
5. The filter element of claim 1 , wherein the web has a basis weight of about 20 g/m 2 to about 300 g/m 2.
6. The filter element of claim 1 , wherein the web has a pore size of about 12 μm to 50 μm.
7. The filter element of claim 1 , wherein the web has a permeability of about 1.5 m/s to 3 m/s.
8. The filter element of claim 1 , wherein the staple fiber comprises a combination of about 1 wt-% to about 20 wt-% of a cellulosic fiber, and about 10 wt-% to about 50 wt-% of a polyester fiber.
9. The filter element of claim 1 , wherein the staple fiber comprises a combination of about 5 wt-% to 15 wt-% of a cotton linter fiber, and about 10 wt-% to about 50 wt-% of a polyester fiber.
10. The filter element of claim 1 , wherein the staple fiber comprises cotton linter fiber having a length of 0.5 mm to 4 mm and diameter of 15 μm to 55 μm.
11. A filter element comprising a filter medium comprising a media layer comprising fibers in a thermally bonded nonwoven web, the web comprising:
(a) about 5 wt-% to 25 wt-%, based on the weight of the web, of a bi-component fiber having a core polymer and a shell polymer, wherein the core polymer has a melting point of at least 240 ° C. and the shell polymer has a melting point of up to 115 ° C.; and the bi-component fiber has a diameter of about 5 μm to about 25 μm and a length of about 2 mm to about 15 mm;
(b) about 25 wt-% to 60 wt-%, based on the weight of the web, of a bi-component fiber having a core polymer and a shell polymer, wherein the core polymer has a melting point of at least 240° C. and the shell polymer has a melting point of 120 ° to 170 ° C.; and the bi-component fiber has a diameter of about 5 μm to about 25 μm and a length of about 2 mm to about 15 mm; and
(c) about 10 wt-% to 70 wt-%, based on the weight of the web, of a staple fiber;
wherein the web has a thickness of about 0.25 mm to about 2 mm, a solidity of under 10 %, a basis weight of about 45 g/m 2 to about 150 g/m 2 , a pore size of about 12 μm to about 50 μm, and a permeability of about 1.5 m/s to about 3 m/s.
12. The filter element of claim 11 , wherein the melting point of the shell polymer of part (b) is about 140 ° C. to about 160 ° C.
13. The filter element of claim 11 , wherein the core polymers of part (a) and part (b) have a melting point of 240° C. to about 260 ° C.
14. The filter element of claim 11 , wherein the web has a basis weight of about 50 g/m 2 to 130 g/m 2 .
15. The filter element of claim 11 , wherein the web is substantially glass free.
16. The filter element of claim 11 , wherein the staple fiber comprises about 15 wt-% to 50 wt-% of the web and comprise a cellulosic fiber or a polyester fiber, or a mixture thereof.
17. The filter element of claim 11 , wherein the staple fiber comprises a combination of about 5 wt-% to 15 wt-% of a cotton linter fiber, and about 10 wt-% to 50 wt-% of a polyester fiber.
18. The filter element of claim 11 , wherein the web has a wet bursting strength of greater than about 5 lb/in 2.
19. A filter element comprising a filter medium comprising a media layer comprising fibers in a thermally bonded nonwoven web, the web comprising:
(a) a bi-component fiber having a structural polymer portion and a thermoplastic binder polymer portion, wherein the structural polymer portion has a melting point of at least 240 ° C. and the binder polymer portion has a melting point of up to 115 ° C.; and the bi-component fiber has a diameter of about 5 μm to 25 μm;
(b) a bi-component fiber having a structural polymer portion and a thermoplastic binder polymer portion, wherein the structural polymer portion has a melting point of at least 240 ° C. and the binder polymer portion has a melting point of 120 ° C. to 170 ° C.; and the bi-component fiber has a diameter of about 5 μm to 25 μm; and
(c) a staple fiber;
wherein the web has a solidity of under 10% and a wet bursting strength of greater than about 5 lb/in 2;
wherein the web comprises about 5 wt-% to 25 wt-%, based on the weight of the web, of the bi-component fiber of part (a); and
wherein the web comprises about 25 wt-% to 60 wt-%, based on the weight of the web, of the bi-component fiber of part (b).
20. The filter element of claim 19 , wherein the wet bursting strength of the web is 10 lb/in 2 to 20 lb/in 2.
21. A filter element comprising a filter medium comprising a media layer comprising fibers in a thermally bonded nonwoven web, the web comprising:
(a) a bi-component fiber having a structural polymer portion and a thermoplastic binder polymer portion, wherein the structural polymer portion has a melting point of at least 240 ° C. and the binder polymer portion has a melting point of about 73 ° C.; and the bi-component fiber has a diameter of about 5 μm to 25 μm and a length of 0.3 cm to 0.9 cm;
(b) a bi-component fiber having a structural polymer portion and a thermoplastic binder polymer portion, wherein the structural polymer portion has a melting point of at least 240 ° C. and the binder polymer portion has a melting point of about 155 ° C.; and the bi-component fiber has a diameter of about 5 μm to 25 μm and a length of 0.3 xm to 0.9 cm; and
(c) a staple fiber;
wherein the web comprises about 5 wt-% to 25 wt-%, based on the weight of the web, of the bi-component fiber of part (a);
wherein the web comprises about 25 wt-% to 60 wt-%, based on the weight of the web, of the bi-component fiber of part (b); and
wherein the web has a solidity of under 10 %.
22. The filter element of claim 21 , wherein the web has a wet bursting strength of greater than about 5 lb/in 2.
23. The filter element of claim 21 , wherein the web has a tensile strength of greater than about 2 lb/in at 100 ° C.