Thin-walled microplate and thermoforming method
Described herein are microplates having wells with ultra-thin walls and methods of forming thereof. The microplates can be made by thermoforming processes that use ultrasound, electricity, etc., to heat a thin polymer sheet or film prior to molding. Vacuum can be optionally applied to help form or shape the wells.
1. A method for manufacturing a microplate comprising a plurality of wells, the method comprising:
preheating, with a film heater, a polymer film having a first film thickness;
advancing, via one or more reels, the preheated polymer film into an embossing device, the embossing device comprising an upper mold and a lower mold;
heating at least one of the upper mold and the lower mold of the embossing device with an ultrasonic heat source to apply heat to the polymer film;
applying a force to the polymer film, via the embossing device, by pressing the polymer film between the upper and lower molds of the embossing device to form the plurality of wells, wherein a first portion of the polymer film corresponds to the plurality of wells and a second portion of the polymer film corresponds to one or more flat portions disposed between the plurality of wells; and
applying a vacuum pressure to the polymer film, via a vacuum channel, to stretch the first portion of the polymer film to form the plurality of wells,
wherein the stretched first portion of the polymer film has a variable thickness and the second portion of the polymer film has a second thickness greater than the variable thickness,
wherein the first film thickness ranges from about 50 microns to about 1000 microns.
2. The method of claim 1 , wherein the polymer film is an extruded polymer film, and wherein the first film thickness is uniform.
3. The method of claim 1 , wherein the plurality of wells have a wall thickness ranging between about 20 to about 120 microns.
4. The method of claim 3 , wherein the plurality of wells have a wall thickness of about 50 microns.
5. The method of claim 1 , further comprising heating, with a heat source, at least one of the upper or lower mold of the embossing device to a temperature ranging from about 80 to about 280 degrees Celsius.
6. The method of claim 1 , further comprising heating, with an ultrasonic heat source, at least one of the upper or lower mold of the embossing device.
7. The method of claim 6 , wherein the ultrasonic heat source produces heat by vibrating at a frequency ranging from about 15 KHz to 40 KHz.
8. The method of claim 1 , wherein the force applied to the polymer film is in a range from about 3.0 to about 6.0 kg.
9. The method of claim 1 , further comprising applying a vacuum force to the polymer film with a pump coupled to the embossing device.
10. The method of claim 9 , wherein the vacuum force applied to the polymer film ranges from about 0.3-0.5 MPa.
11. The method of claim 1 , wherein the polymer film comprises a thermoplastic polymer.
12. The method of claim 1 , wherein the microplate comprises an array of the plurality of wells.
13. The method of claim 1 , wherein a volume of each of the plurality of wells has a coefficient of variation value ranging from about 3% to about 5%.
14. A method for manufacturing a microplate comprising a plurality of wells, the method comprising:
preheating, with a film heater, a polymer film;
advancing, via one or more reels, the preheated polymer film into an embossing device, the embossing device comprising an upper mold and a lower mold;
heating at least one of the upper mold and the lower mold of the embossing device with an ultrasonic heat source to apply heat to the polymer film;
applying a force to the polymer film, via the embossing device, by pressing the polymer film between the upper and lower molds of the embossing device to form the plurality of wells, wherein a first portion of the polymer film corresponds to the plurality of wells and a second portion of the polymer film corresponds to one or more flat portions disposed between the plurality of wells; and
applying a vacuum pressure to the polymer film, via a vacuum channel, to stretch the first portion of the polymer film to form the plurality of wells,
wherein the stretched first portion of the polymer film has a variable thickness and the second portion of the polymer film has a second thickness greater than the variable thickness.