Vapor permeable, water resistive, air barrier polyester membrane having a polyacrylic coating with porous pressure sensitive adhesive added to the rear surface of the membrane
An ultra violet stable polyester membrane with a polyacrylic coating on one side and a coated pressure sensitive adhesive coating on its other side capable of allowing water vapor to pass through it. The pressure sensitive adhesive is formed of a copolymer comprising a backbone of n-butyl acrylate, 2-ethylhexyl acrylate, and vinyl acetate which is mixed with at least one surfactant and emulsified to produce air bubbles which form pores when the copolymer is set with about 80% to about 90% of the pore sizes ranging from about 200 microns to about 300 microns and being uniformly distributed to form a flow path through the pressure sensitive adhesive.
1. A water resistive building membrane comprising:
at least one permeable polyester plastic sheet having a front face,
a polyacrylic coating coating the sheet's front face,
a coating of permeable pressure sensitive acrylic; adhesive applied to an outer surface of the sheet opposite the sheet's front face, wherein the permeable pressure sensitive acrylic; adhesive comprises:
at least 4000 entrained interconnected pores per square inch of adhesive, of which at least 80% of the pores have a size ranging from about 200 microns to about 300 microns, the pores being uniformly distributed and interconnected throughout the adhesive to form a water resistive water vapor flow path through the adhesive such that the adhesive has a vapor permeability of at least 40 Perms, and
a copolymer with a backbone of n-butyl acrylate, 2-ethylhexyl acrylate, and vinyl acetate.
2. A water resistive building membrane as claimed in claim 1 wherein the pressure sensitive porous adhesive has a vapor permeability ranging from 40 to 70 Perms.
3. A water resistive building membrane as claimed in claim 1 wherein said pressure sensitive adhesive has a density ranging between about 0.65 to about 0.75.
4. A water resistive building membrane as claimed in claim 1 wherein said pressure sensitive adhesive has a pore density which ranges from 4000 per in 2 to about 4600 per in 2 .
5. A water resistive building membrane as claimed in claim 1 wherein said pressure sensitive adhesive has a pore density of about 4400 per in 2 .
6. A water resistive building membrane as claimed in claim 1 wherein said pressure sensitive adhesive contains a flame-retardant material.
7. A water resistive building membrane as claimed in claim 6 wherein said flame retardant material is Antimony Oxide.
8. A water resistive building membrane as claimed in claim 6 wherein said flame retardant material is taken from a group consisting of halogenated fire suppressants, hydrated inorganic compounds selected from one of the following aluminum trihydrate, magnesium hydroxide, calcium borate and zinc borate, intumescent phosphate, ammonium polyphosphate, organic and inorganic phosphate compounds selected from one of the following ammonium sulfate, sulfamate compounds and free radical scavenger materials.
9. A water resistive building membrane as claimed in claim 6 wherein said flame retardant material is present in said pressure sensitive adhesive in a range of about 0.5% by weight to about 3% by weight.
10. A water resistive building membrane as claimed in claim 6 wherein said pressure sensitive adhesive contains a flame-retardant material in a range of about 2% by weight to about 3% by weight.
11. A water resistive building membrane comprising:
a permeable polyester sheet with a polyacrylic coating, and
a coating of permeable pressure sensitive adhesive applied to an outer surface of the sheet, wherein the permeable pressure sensitive acrylic adhesive comprises:
at least 4000 entrained interconnected pores per square inch of adhesive, of which at least 80% of the pores have a size ranging from about 200 microns to about 300 microns, the pores having a rounded shape and being uniformly distributed and interconnected throughout the adhesive to form a water resistive water vapor flow path through the adhesive, and
a copolymer with a backbone of n-butyl acrylate, 2-ethylhexyl acrylate, and vinyl acetate.
12. A water resistive building membrane as claimed in claim 11 wherein said pressure sensitive adhesive contains a flame-retardant material.
13. A water resistive building membrane as claimed in claim 11 wherein a release liner is placed on said pressure sensitive adhesive material.
14. A water resistive membrane as claimed in claim 11 wherein said pressure sensitive adhesive has a density ranging between about 0.65 and about 0.75 after aeration.
15. The membrane of claim 11 wherein the permeable pressure sensitive acrylic adhesive has a vapor permeability of at least 40 Perms.