Coating-liquid-impregnated fiber-reinforced fabric, sheet-shaped integrated object, prepreg, prepreg tape, and method for manufacturing fiber-reinforced composite material
The present invention is a method of producing a coating liquid-impregnated reinforcing fiber fabric 1 b , including allowing a reinforcing fiber fabric 1 a to pass substantially vertically downward through the inside of a coating section 20 storing a coating liquid 2 to provide the reinforcing fiber fabric 1 a with the coating liquid 2 ; wherein the coating section 20 includes a liquid pool and a narrowed section which are in communication with each other; wherein the liquid pool has a portion whose cross-sectional area decreases continuously along a running direction of the reinforcing fiber fabric 1 a , wherein the narrowed section has a slit-like cross-section and has a smaller cross-sectional area than the top side of the liquid pool, and wherein the vertical height of the portion whose cross-sectional area decreases continuously in the liquid pool is 10 mm or more.
1. A method of producing a coating liquid-impregnated sheet-shaped reinforcing fiber fabric, comprising:
allowing a sheet-shaped reinforcing fiber fabric to pass substantially vertically downward through the inside of a coating section storing a coating liquid to provide said reinforcing fiber fabric with said coating liquid;
wherein said coating section includes a liquid pool and a narrowed section which are in communication with each other;
wherein said liquid pool has a portion whose cross-sectional area decreases continuously along a running direction of said reinforcing fiber fabric;
wherein said narrowed section has a slit-shaped cross-section and has a smaller cross-sectional area than the top side of said liquid pool;
wherein the vertical height of said portion whose cross-sectional area decreases continuously in said liquid pool is 10 mm or more, and
wherein said coating section further comprises, in said liquid pool, a width regulation mechanism for regulating the width of said reinforcing fiber fabric, wherein the relationship between the width (W) of said reinforcing fiber fabric immediately under said narrowed section and the width (L 2 ) regulated by said width regulation mechanism at the lower end of said width regulation mechanism satisfies L 2 ≤W+10 (mm).
2. The method of producing a coating liquid-impregnated sheet-shaped reinforcing fiber fabric according to claim 1 , wherein said width regulation mechanism is provided over the whole region of said liquid pool and said narrowed section.
3. The method of producing a coating liquid-impregnated sheet-shaped reinforcing fiber fabric according to claim 1 , wherein the viscosity of said coating liquid is 1 to 60 Pas as measured at a strain rate of 3.14 s −1 at a coating liquid temperature in said liquid pool.
4. The method of producing a coating liquid-impregnated sheet-shaped reinforcing fiber fabric according to claim 1 , wherein said coating liquid contains a thermosetting resin.
5. The method of producing a coating liquid-impregnated sheet-shaped reinforcing fiber fabric according to claim 1 , comprising:
using a coating liquid containing polymer particles; and
providing said reinforcing fiber fabric with said coating liquid,
wherein the temperature of said coating liquid in said coating section is 20° C. or more lower than the glass transition temperature (Tg) or melting point (Tm) of a resin constituting said polymer particles.
6. The method of producing a coating liquid-impregnated sheet-shaped reinforcing fiber fabric according to claim 1 , wherein said reinforcing fiber fabric is heated and then introduced into said liquid pool.
7. A method of producing a sheet-shaped integrated object, comprising:
obtaining a coating liquid-impregnated sheet-shaped reinforcing fiber fabric by said method of producing a coating liquid-impregnated reinforcing fiber fabric according to claim 1 ;
providing at least one side of the obtained coating liquid-impregnated reinforcing fiber fabric with a release sheet to form a sheet-shaped integrated object; and
taking up said sheet-shaped integrated object.
8. The method of producing a sheet-shaped integrated object according to claim 7 , wherein said sheet-shaped integrated object is formed and then subjected to after-impregnation.
9. The method of producing a sheet-shaped integrated object according to claim 7 , wherein said sheet-shaped integrated object is a prepreg.
10. A method of producing a prepreg tape, comprising:
obtaining a prepreg by said method of producing a sheet-shaped integrated object according to claim 9 ; and
slitting said prepreg.
11. A method of producing a fiber reinforced composite material, comprising:
obtaining a prepreg by said method of producing a sheet-shaped integrated object according to claim 9 ; and
curing said prepreg.
12. A method of producing a fiber reinforced composite material, comprising:
obtaining a prepreg tape by said method of producing a prepreg tape according to claim 10 ; and
curing said prepreg tape.