Self-fusing silicone tape compositions having corrosion inhibitors therein
Self-fusing silicone tapes contain neutral corrosion inhibitors therein such as salts of acids. Such tapes provide protection in an acid gas environment as well as under thermal insulation. The same also allows inspection of protected structure without removing the protection apparatus.
1. A mixture, comprising: a self-fusing polysiloxane composition, and a non alkaline, water soluble neutral corrosion inhibitor, said self-fusing polysiloxane composition capable of being fused to itself and become an integral, flexible mass; from about 0.1 to about 25 parts by weight of said non alkaline, water soluble neutral corrosion inhibitor for every 100 parts by weight of said self-fusing polysiloxane composition, said non alkaline, water soluble neutral corrosion inhibitor comprising a salt of a phosphoric acid, a salt of a gluconic acid, a salt of a carboxylic acid, a salt of benzoic acid, or an aluminum magnesium carbonate hydroxide, or any combination thereof; wherein said corrosion inhibitors have a pH of from about 5.5 to about 8.5; wherein said water soluble neutral corrosion inhibitor is capable of being transferred to a metal surface via moisture, and wherein said self-fusing polysiloxane provides corrosion protection in an acid gas environment.
2. The mixture according to claim 1 , wherein said self-fusing polysiloxane composition further comprises a crosslinking agent.
3. The mixture according to claim 2 , wherein said polysiloxane is one or more of FMQ, FVMQ, PMQ, PVMQ, MQ, r VMQ, or any combination thereof, and wherein said corrosion inhibitors have a pH of from about 6.5 to about 7.5.
4. The mixture according to claim 1 , wherein said non alkaline, water soluble corrosion inhibitor salts comprise sodium hexameta phosphate, calcium phosphate dibasic, sodium calcium polyphosphate, sodium benzoate, calcium benzoate, or sodium gluconate, or any combination thereof.
5. The mixture according to claim 4 , wherein the amount of said non alkaline, water soluble corrosion inhibitor salt is from about 0.25 parts to about 10 parts by weight for every 100 parts by weight of said self-fusing polysiloxane composition.
6. The mixture according to claim 5 , wherein the particle size of said non alkaline, water soluble corrosion inhibitor salt is less than about 0.006 inches; and wherein said corrosion inhibitors have a pH of from about 6 to about 8.
7. The mixture according to claim 4 , wherein said non alkaline, water soluble corrosion inhibitor salt comprises sodium benzoate, and wherein the amount of said sodium benzoate is from about 0.25 parts to about 3.5 parts by weight for every 100 parts by weight of said self-fusing polysiloxane composition.
8. The mixture according to claim 7 , wherein the particle size of said non alkaline, water soluble corrosion inhibitors is less than about 0.005 inches.
9. The mixture according to claim 4 , wherein said non alkaline, water soluble corrosion inhibitor comprises sodium benzoate, wherein the amount of any alkaline corrosion inhibitor is about 1.0 part by weight or less for every 100 parts by weight of said self-fusing polysiloxane composition, and further comprising a metal surface, whereby said water solubility of said corrosion inhibitor aids in the transfer of said inhibitor to said metal surface.
10. The mixture according to claim 9 , wherein the amount of any alkaline corrosion inhibitor is about 0.5 part by weight or less for every 100 parts by weight of said self-fusing polysiloxane composition, and wherein the amount of any non-fusing polymer, or rubber, or both, is about 2.5 parts by weight or less for every 100 parts by weight of said self-fusing polysiloxane composition.
11. The mixture according to claim 9 , wherein the amount of any alkaline corrosion inhibitor is about 0.5 part by weight or less for every 100 parts by weight of said self-fusing polysiloxane composition.
12. The mixture according to claim 9 , wherein the amount of any water insoluble salt is about 10 parts by weight or less per 100 parts by weight of said self-fusing silicone tape composition.
13. The mixture according to claim 9 , wherein the amount of any water insoluble salt is about 5 parts by weight or less per 100 parts by weight of said self-fusing silicone tape composition.
14. The mixture according to claim 9 , wherein the amount of any water insoluble salt is about 2 parts by weight or less per 100 parts by weight of said self-fusing silicone tape composition.