Optical article with high reflection in the near infrared region and in the blue light region

1. An optical article comprising a transparent substrate with a front main face and a rear main face, at least one of the main faces being coated with an antireflective coating comprising at least two layers having a low refractive index, which is <1.55, each defined as an “LI layer”, and at least two layers having a high refractive index, which is 1.55, each defined as an “HI layer”, one of the at least two HI layers being the layer which is the nearest from said substrate among said LI and HI layers, wherein a layer of the antireflective coating is defined as having a thickness higher than or equal to 1 nm, said HI and LI layers do not need to alternate with each other, provided that when the antireflective coating includes alternating HI and LI layers, at least one HI layer may be made of a doublet or a triplet, a doublet is made from the deposition of a first high refractive index material on which a second high refractive index material is directly deposited, and a triplet is made from the deposition of a first high refractive index material on which a second high refractive index material is directly deposited, on which a third high refractive index material is directly deposited, wherein the total physical thickness of said antireflective coating is equal to or lower than 600 nm, and wherein the antireflection coating is configured such that:

the mean reflection factor in the near infrared (NIR) region R m NIR is higher than or equal to 20% at an angle of incidence lower than 35°; and

the mean reflection factor R m B of blue light at a wavelength ranging from 420 to 450 nm has a first value R m B (<15°) which is higher than or equal to 7.0% at an angle of incidence lower than 15°, and

the mean light reflection factor in the visible region R v is lower than or equal to 2.0% for at least an angle of incidence lower than 35°, and

wherein the mean reflection factor R m B of blue light at a wavelength ranging from 420 to 450 nm has a second value R m B (35°) at an angle of incidence of 35° which fulfills following condition: R m B (<15°) −R m B (35°) ≥5%.

2. The optical article of claim 1 , wherein the mean light reflection factor in the visible region R v of said antireflective coating is lower than or equal to 1.5% for at least an angle of incidence lower than 35°.

3. The optical article of claim 2 , wherein the mean light reflection factor in the visible region R v of said antireflective coating is lower than or equal to 1.0% for at least an angle of incidence lower than 35°.

4. The optical article of claim 1 , wherein the mean reflection factor in the near infrared (NIR) region R m NIR of said antireflective coating is higher than or equal to 25% at an angle of incidence lower than 35°.

5. The optical article of claim 4 , wherein the mean reflection factor in the near infrared (NIR) region R m NIR of said antireflective coating is higher than or equal to 26% at an angle of incidence lower than 35°.

6. The optical article of claim 5 , wherein the mean reflection factor in the near infrared (NIR) region R m NIR of said antireflective coating is higher than or equal to 30% at an angle of incidence lower than 35°.

7. The optical article of claim 1 , wherein the antireflective coating has a Chroma C* which is higher or equal to 20 of the international colorimetric system CIE L*a*b*.

8. The optical article of claim 7 , wherein the antireflective coating has a Chroma C* which is higher or equal to 25 of the international colorimetric system CIE L*a*b*.

9. The optical article of claim 8 , wherein the antireflective coating has a Chroma C* which is higher or equal to 30 of the international colorimetric system CIE L*a*b*.

10. The optical article of claim 1 , wherein the sum of physical thickness of all HI layers is ranging from 190 nm to 265 nm.

11. The optical article of claim 10 , wherein the sum of physical thickness of all HI layers is ranging from 195 nm to 260 nm.

12. The optical article of claim 1 , wherein the number of layers of said antireflective coating is lower than or equal to 8.

13. The optical article of claim 1 , wherein the layer which is the farthest from the substrate of said antireflective coating is a LI layer having a physical thickness ranging from 55 to 95 nm.

14. The optical article of claim 13 , wherein the layer which is the farthest from the substrate of said antireflective coating is a LI layer having a physical thickness ranging from 60 to 92 nm.

15. The optical article of claim 1 , wherein said antireflective coating comprises in the direction moving away from the substrate, the following layers which are in direct contact with each other: (1) an HI layer/(2) a LI layer/(3) an HI layer/and (4) a LI layer.

16. The optical article of claim 15 , wherein the (1) HI layer, the (3) HI layer or both the (1) HI layer and the (3) HI layer of said antireflective coating is a doublet (bilayer) or a triplet (trilayer) made of distinct metal oxides.

17. The optical article of claim 15 , wherein said antireflective coating comprises in the direction moving away from the substrate a:

HI layer having a physical thickness ranging from 130 to 160 nm;

LI layer having a physical thickness ranging from 140 to 215 nm;

HI layer having a physical thickness ranging from 90 to 130 nm; and

LI layer having a physical thickness ranging from 60 to 90 nm.

18. The optical article of claim 1 , wherein said antireflective coating comprises in the direction moving away from the substrate, the following layers which are in direct contact with each other: (1) a HI layer/(2) a LI layer/(3) a HI layer/(4) a LI layer, (5) a HI layer/and (6) a LI layer.

19. The optical article of claim 18 , wherein said antireflective coating comprises in the direction moving away from the substrate a:

(1) HI layer having a physical thickness ranging from 15 to 60 nm;

(2) LI layer having a physical thickness ranging from 8 to 25 nm;

(3) HI layer having a physical thickness ranging from 80 to 120 nm;

(4) LI layer having a physical thickness ranging from 170 to 195 nm;

(5) HI layer having a physical thickness ranging from 80 to 120 nm; and

(6) LI layer having a physical thickness ranging from 70 to 95 nm.

20. The optical article of claim 18 , wherein said antireflective coating comprises in the direction moving away from the substrate a:

HI layer having a physical thickness ranging from 15 to 22 nm;

LI layer having a physical thickness ranging from 10 to 25 nm;

HI layer having a physical thickness ranging from 80 to 115 nm;

LI layer having a physical thickness ranging from 170 to 185 nm;

HI layer having a physical thickness ranging from 85 to 95 nm; and

LI layer having a physical thickness ranging from 75 to 90 nm.

21. The optical article of claim 1 , wherein said optical article is an ophthalmic lens.