Thermally conductive silicone composition
With respect to an addition-curable thermally conductive silicone composition in which a silver filler is blended, a catalyst having a specific structure and an organohydrogen polysiloxane having a specific structure are used for the purpose of extending the working life at room temperature, while maintaining the flexibility, so that a thermally conductive silicone composition which is able to have a good balance between flexibility after curing and storage stability in one pack, while having extremely low thermal resistance and excellent reliability is achieved.
1. A heat-conductive silicone composition comprising the following components (A) to (D):
(A) 100 parts by weight of an organopolysiloxane containing at least two alkenyl groups per molecule and having a kinematic viscosity of 10 to 100,000 mm 2 /s at 25° C.,
(B) an organohydrogenpolysiloxane containing at least two silicon-bonded hydrogen atoms (i.e., Si—H groups) per molecule and free of molecular end Si—H groups, in such an amount that the number of Si—H groups in component (B) divided by the number of alkenyl groups in component (A) falls in the range from 1.5 to 2.5,
(C) a platinum complex curing catalyst selected from the group consisting of trimethyl(acetylacetonato)platinum complex, trimethyl(2,4-pentanedionato)platinum complex, trimethyl(3,5-heptanedionato)platinum complex, trimethyl(methylacetoacetato)platinum complex, bis(2,4-pentanedionato)platinum complex, bis(2,4-hexanedionato)platinum complex, bis(2,4-heptanedionato)platinum complex, bis(3,5-heptanedionato)platinum complex, bis(1-phenyl-1,3-butanedionato)platinum complex, bis(1,3-diphenyl-1,3-propanedionato)platinum complex, (1,5-cyclooctadienyl)dimethyl platinum complex, (1,5-cyclooctadienyl)diphenyl platinum complex, (1,5-cyclooctadienyl)dipropyl platinum complex, (2,5-norbornadiene)dimethyl platinum complex, (2,5-norbornadiene)diphenyl platinum complex, (cyclopentadienyl)dimethyl platinum complex, (methylcyclopentadienyl)diethyl platinum complex, (trimethylsilylcyclopentadienyl)diphenyl platinum complex, (methylcycloocta-1,5-dienyl)diethyl platinum complex, (cyclopentadienyl)trimethyl platinum complex, (cyclopentadienyl)ethyldimethyl platinum complex, (cyclopentadienyl)acetyldimethyl platinum complex, (methylcyclopentadienyl)trimethyl platinum complex, (methylcyclopentadienyl)trihexyl platinum complex, (trimethylsilylcyclopentadienyl)trimethyl platinum complex, (dimethylphenylsilylcyclopentadienyl)triphenyl platinum complex, and (cyclopentadienyl)dimethyltrimethylsilylmethyl platinum complex, in such an amount as to give 500 to 10,000 ppm of platinum atom based on the weight of component (A), and
(D) 500 to 3,000 parts by weight of silver powder.
2. The heat-conductive silicone composition of claim 1 , further comprising (E) a heat-conductive filler having a thermal conductivity of at least 10 W/m° C. other than component (D), in an amount of 1 to 300 parts by weight per 100 parts by weight of component (A).
3. The heat-conductive silicone composition of claim 1 , further comprising (F) an inhibitor selected from acetylene compounds, nitrogen compounds, organic phosphorus compounds, oxime compounds, and organic chlorine compounds, in an amount of 0.05 to 0.5 part by weight per 100 parts by weight of component (A).
4. The heat-conductive silicone composition of claim 1 , further comprising (G) an organosilane having the general formula (1):
R 1 a R 2 b Si(OR 3 ) 4-a-b (1)
wherein R 1 is a C 9 -C 15 alkyl group, R 2 is a C 1 -C 10 monovalent hydrocarbon group, R 3 is at least one C 1 -C 6 alkyl group, a is an integer of 1 to 3, b is 0, 1 or 2, and a+b is an integer of 1 to 3, in an amount of 1 to 10 parts by weight per 100 parts by weight of component (A).
5. The heat-conductive silicone composition of claim 1 , further comprising (H) a one end trifunctional hydrolyzable methylpolysiloxane having the general formula (2):
wherein R 4 is a C 1 -C 6 alkyl group and c is an integer of 5 to 100, in an amount of 1 to 10 parts by weight per 100 parts by weight of component (A).