Polybutylene terephthalate resin composition and molded article
A polybutylene terephthalate resin composition containing a polybutylene terephthalate resin, a silicone-based compound having a kinematic viscosity at 25° C. of 1,000 to 10,000 cSt in an amount of 0.5 to 1.8% by mass of the total mass of the polybutylene terephthalate resin composition, and an olefin-based elastomer in an amount of 5 to 20% by mass of the total mass of the polybutylene terephthalate resin composition.
1. A polybutylene terephthalate resin composition comprising:
a polybutylene terephthalate resin,
a silicone-based compound having a kinematic viscosity at 25° C. of 3,000 to 6,000 cSt, in an amount of 0.5 to 1.3% by mass of a total mass of the polybutylene terephthalate resin composition, and
an olefin-based elastomer in an amount of 5 to 20% by mass of a total mass of the polybutylene terephthalate resin composition, wherein the olefin-based elastomer comprises an ethylene-ethyl acrylate copolymer.
2. The polybutylene terephthalate resin composition according to claim 1 , wherein the silicone-based compound comprises a dimethylpolysiloxane.
3. The polybutylene terephthalate resin composition according to claim 1 , further comprising a filler in an amount of 10 to 50% by mass of a total mass of the polybutylene terephthalate resin composition.
4. The polybutylene terephthalate resin composition according to claim 3 , wherein the filler comprises glass fiber.
5. A molded article molded using the polybutylene terephthalate resin composition according to claim 1 .
6. The molded article according to claim 5 , wherein the molded article is an insert molded article comprising an insert member containing at least one selected from the group consisting of a metal and an inorganic solid.
7. The molded article according to claim 5 , wherein the molded article is used in a component that makes contact with an alkali solution.
8. The polybutylene terephthalate resin composition according to claim 1 , wherein the polybutylene terephthalate resin composition consists of the polybutylene terephthalate resin, the silicone-based compound, the olefin-based elastomer, and at least one selected from the group consisting of a filler, an antioxidant, a stabilizer, a molecular weight adjuster, an ultraviolet absorber, an antistatic agent, a colorant, a lubricant, a mold release agent, a crystallization promoter, a crystal nucleating agent, an infrared absorber, a flame retardant assistant, a hydrolysis resistance improver, and a fluidity improver.