Process for casting aluminum alloy parts
A process for casting aluminum alloy parts is disclosed. The process includes the steps as follows: raising a liquid aluminum alloy; filling a mold; increasing pressure; solidifying formed by at least two stages of different pressure settings; and relieving pressure.
1. A process for casting an aluminum alloy part, comprising the following consecutive steps in a single cycle of casting:
raising a liquid aluminum alloy;
filling a mold;
increasing pressure;
solidifying consisting of at least two stages of different pressure settings; and
relieving pressure,
wherein the step of solidifying is independent of the step of relieving pressure,
wherein the step of solidifying consisting of at least two stages of different pressure settings comprises the following steps:
a first high pressure solidifying stage, comprising: increasing a pressure in a mold cavity to 1400-1800 Mbar at a rate of 100-200 Mbar/s, maintaining the pressure for 3-8 s, and then reducing the pressure in the mold cavity to 700-1100 Mbar at a rate of 100-200 Mbar/s;
a first low pressure solidifying stage;
a second high pressure solidifying stage, comprising: increasing the pressure in the mold cavity to 1500-3000 Mbar at a rate of 120-250 Mbar/s, maintaining the pressure for 3-12 s, and then reducing the pressure in the mold cavity to 700-1100 Mbar at a rate of 120-250 Mbar/s;
a second low pressure solidifying stage;
a third high pressure solidifying stage, comprising: increasing the pressure in the mold cavity to 3000-4500 Mbar at a rate of 120-250 Mbar/s, maintaining the pressure for 3-12 s, and then reducing the pressure in the mold cavity to 700-1100 Mbar at a rate of 120-250 Mbar/s; and
a third low pressure solidifying stage.
2. The process for casting an aluminum alloy part according to claim 1 , wherein the first low pressure solidifying stage, the second low pressure solidifying stage and the third low pressure solidifying stage each comprise:
maintaining the pressure in the mold cavity at 700-1100 Mbar for a preset time.
3. The process for casting an aluminum alloy part according to claim 1 , wherein the step of raising the liquid aluminum alloy comprises:
increasing a pressure of the liquid aluminum alloy in a crucible to 200 Mbar at a rate of 10-30 Mbar/s.
4. The process for casting an aluminum alloy part according to claim 1 , wherein the step of filling the mold comprises:
increasing a pressure of the liquid aluminum alloy to 360 Mbar at a rate of 5-15 Mbar/s.
5. The process for casting an aluminum alloy part according to claim 1 , wherein the step of increasing pressure comprises:
increasing the pressure in the mold cavity to 700-1100 Mbar at a rate of 40-80 Mbar/s.
6. The process for casting an aluminum alloy part according to claim 1 , wherein the step of relieving pressure comprises:
reducing the pressure in the mold cavity to 0 Mbar from 700-1100 Mbar.