Laminate, blister pack, press-through package, and laminate manufacturing method
A laminate has a substrate layer, an intermediate layer, and a fluorine-based resin layer in that order, in which the substrate layer contains any one or more kinds of a polyolefin-based resin, a polyester-based resin or a vinyl-based resin, the intermediate layer contains a polyethylene resin and a modified polyethylene resin, and the intermediate layer has a thickness of 5 μm or more and 50 μm or less.
1. A laminate consisting essentially of a substrate layer, an intermediate layer, a fluorine-based resin layer, a second intermediate layer, and a second substrate layer in that order, wherein
said substrate layer contains any one or more kinds of a polyolefin-based resin, a polyester-based resin or a vinyl-based resin,
said substrate layer has a thickness of 45 μm or more and 100 μm or less, a thickness of said second substrate layer relative to a thickness of said substrate layer is 0.95 times to 1.05 times,
each of said intermediate layer and said second intermediate layer consists essentially of a linear low density polyethylene and a maleic anhydride-modified polyethylene,
a mixing ratio of the linear low density polyethylene and the maleic anhydride-modified polyethylene is 20:80 to 50:50,
said intermediate layer has a thickness of 5 μm or more and 50 μm or less,
a thickness of said second intermediate layer relative to a thickness of said intermediate layer is 0.9 times to 1.1 times,
said fluorine-based resin layer contains polychlorotrifluoroethylene,
said fluorine-based resin layer has a thickness of 40 μm or more and 150 μm or less, and
said laminate has a water vapor permeability of 0.5 g/m 2 /24 hours or less.
2. The laminate according to claim 1 , wherein said intermediate layer has a thickness of 10 μm or more and 30 μm or less.
3. A blister container comprising the laminate according to claim 1 .
4. A press-through package comprising the laminate according to claim 1 .
5. A method for manufacturing the laminate according to claim 1 , the method comprising a step of simultaneously melt extrusion-molding a resin to be a raw material of said substrate layer, a resin to be a raw material of said intermediate layer, a resin to be a raw material of said fluorine-based resin layer, a resin to be a raw material of said second intermediate layer, and a resin to be a raw material of said second substrate layer.