Modified conjugated diene-based polymer, polymer composition, and rubber composition
A modified conjugated diene-based polymer according to the present invention has a weight average molecular weight of 20×10 4 or more and 300×10 4 or less, has a molecular weight distribution Mw/Mn of 1.6 or more and 4.0 or less, has a modification ratio of 30% by mass or more and 80% by mass or less with respect to a total amount of the conjugated diene-based polymer, and includes 5% by mass or more and 50% by mass or less of a component having a molecular weight of 1,000,000 or more and 5,000,000 or less in GPC (gel permeation chromatography), wherein a modification ratio of the component having a molecular weight of 1,000,000 or more and 5,000,000 or less is 90% by mass or more and 100% by mass or less.
1. A modified conjugated diene-based polymer, wherein the modified conjugated diene-based polymer
has a weight average molecular weight of 20×10 4 or more and 300×10 4 or less,
has a molecular weight distribution Mw/Mn of 1.6 or more and 4.0 or less,
has a modification ratio of 30% by mass or more and 80% by mass or less with respect to a total amount of the conjugated diene-based polymer, and
comprises 5% by mass or more and 50% by mass or less of a component having a molecular weight of 1,000,000 or more and 5,000,000 or less in GPC (gel permeation chromatography), wherein
a modification ratio of the component having a molecular weight of 1,000,000 or more and 5,000,000 or less is 90% by mass or more and 100% by mass or less.
2. The modified conjugated diene-based polymer according to claim 1 , wherein
a modification ratio of a molecular weight component with a peak top, or a peak top of the largest molecular weight among molecular weights of a plurality of peaks, if present, in GPC is 1.10 times or more a modification ratio of the whole modified conjugated diene-based polymer.
3. The modified conjugated diene-based polymer according to claim 1 , wherein
a modification ratio of a molecular weight component having ½ of a molecular weight at a peak top, or a peak top of the largest molecular weight among molecular weights of a plurality of peaks, if present, in GPC is ½ or less of a modification ratio of the whole modified conjugated diene-based polymer.
4. The modified conjugated diene-based polymer according to claim 1 , wherein
Mw/Mn in GPC is 2.0 or more and 4.0 or less, and
shrinkage factor g′ is 0.64 or more and 1.00 or less.
5. The modified conjugated diene-based polymer according to claim 1 , wherein
the modified conjugated diene-based polymer comprises 3 mass ppm or more each of nitrogen and silicon, wherein
a molar ratio of nitrogen to silicon (nitrogen/silicon) is 1.1 or more and less than 10.
6. The modified conjugated diene-based polymer according to claim 1 , wherein
the modified conjugated diene-based polymer comprises 3 mass ppm or more each of nitrogen and silicon, wherein
a molar ratio of nitrogen to silicon (nitrogen/silicon) is 0.1 or more and less than 0.9.
7. A polymer composition comprising 10% by mass or more of the modified conjugated diene-based polymer according to claim 1 .
8. A rubber composition comprising
100 parts by mass of a rubber-like polymer comprising 10% by mass or more of the modified conjugated diene-based polymer according to claims 1 , and
5 to 150 parts by mass of a filler.