Method for producing a single-sided adhesive film and single-sided adhesive film
The invention relates to a method for producing a single-sided adhesive film ( 1 ). Said method consists of providing a support layer ( 2 ) and coating a first side of the support layer ( 2 ) with an adhesive film ( 3 ), a lubricant coating ( 4 ) is applied to a second side of the support layer ( 2 ), the support layer ( 2 ) being in the form of a polyester film. Said method is characterised in that the polyester film, prior to bonding to the adhesive layer ( 3 ), and the lubricant coating ( 4 ) is treated with trichloroacetic acid, sodium persulphate, iron chloride or copper chloride in order to increase the surface energy of the polyester film. The invention also relates to a one-sided adhesive film ( 1 ) produced according to the above-mentioned method.
1. A method for producing a single-sided adhesive film, comprising:
providing a backing layer, and
coating a first side of the backing layer with an adhesive layer,
wherein a slip coating is applied to a second side of the backing layer, and
wherein the backing layer is provided in the form of a polyester film,
characterized in that prior to bonding to the adhesive layer and the slip coating, the polyester film is treated with trichloroacetic acid, sodium persulfate, iron chloride or copper chloride in order to increase the surface energy of the polyester film,
wherein the slip coating comprises polyurethane and is directly sprayed onto the second side of the backing layer so that the slip coating is planar.
2. The method as claimed in claim 1 , characterized in that the slip coating hardens on the backing layer and is thus fixed to the backing layer.
3. The method as claimed in claim 1 , characterized in that a release film is applied to the side of the adhesive layer facing away from the backing layer.