Resin composition, molded article, food contact appliance and food contact container
A resin composition is provided. The resin composition includes a styrene-acrylonitrile based copolymer of 75 parts by weight to 90 parts by weight and rubber particles of 10 parts by weight to 25 parts by weight. The resin composition includes an oligomer trimer. The oligomer trimer includes at least one monomer unit selected from the group consisting of a styrene based monomer unit and an acrylonitrile based monomer unit. Wherein, a residual acrylonitrile based monomer is less than 5 ppm of the total weight of the resin composition. The ratio of the peak area of acetophenone to the peak area of air for the resin composition as analyzed by a thermal desorption gas chromatography mass spectrometer (TD-GC-MS) is 100 to 300.
1. A resin composition, comprising:
a styrene-acrylonitrile based copolymer, which is in an amount of 80 parts by weight to 85 parts by weight; and
graft polymerized rubber particles, which are in an amount of 15 parts by weight to 20 parts by weight,
wherein the resin composition comprises an oligomer trimer, and the oligomer trimer comprises at least one monomer unit selected from the group consisting of a styrene based monomer unit and an acrylonitrile based monomer unit,
wherein a residual acrylonitrile based monomer is less than 5 ppm of a total weight of the resin composition,
wherein a ratio of a peak area of acetophenone to a peak area of air for the resin composition as analyzed by a thermal desorption gas chromatography mass spectrometer (TD-GC-MS) is 100 to 300, and
wherein a content of the oligomer trimer is a value between 4000 ppm to 7000 ppm of the total weight of the resin composition.
2. The resin composition according to claim 1 , wherein the content of the oligomer trimer is a value between 4000 ppm to 6800 ppm of the total weight of the resin composition.
3. The resin composition according to claim 1 , wherein the content of the oligomer trimer is a value between 4000 ppm to 6500 ppm of the total weight of the resin composition.
4. The resin composition according to claim 1 , wherein a styrene based monomer unit of the styrene-acrylonitrile based copolymer is 65% to 80% by weight based on a total weight of the styrene-acrylonitrile based copolymer, and an acrylonitrile based monomer unit is 20% to 35% by weight based on a total weight of the styrene-acrylonitrile based copolymer.
5. The resin composition according to claim 1 , wherein a styrene based monomer unit of the styrene-acrylonitrile based copolymer is 70% to 75% by weight based on a total weight of the styrene-acrylonitrile based copolymer, and an acrylonitrile based monomer unit is 25% to 30% by weight based on a total weight of the styrene-acrylonitrile based copolymer.
6. The resin composition according to claim 1 , wherein the styrene-acrylonitrile based copolymer has a weight average molecular weight of 100,000 to 150,000.
7. The resin composition according to claim 1 , wherein the styrene-acrylonitrile based copolymer has a weight average molecular weight of 120,000 to 130,000.
8. The resin composition according to claim 1 , wherein the styrene-acrylonitrile based copolymer is a styrene-acrylonitrile copolymer.
9. The resin composition according to claim 1 , wherein the styrene-acrylonitrile based copolymer is obtained by extrusion granulation with a biaxial extruder, and an operating temperature of the biaxial extruder is from 220° C. to 240° C., and an operating pressure is from 20 torr to 30 torr.
10. The resin composition according to claim 1 , wherein the graft polymerized rubber particles are diene based rubber particles.
11. The resin composition according to claim 10 , wherein the diene based rubber is a butadiene rubber.
12. The resin composition according to claim 1 , wherein a weight-mean diameter of the graft polymerized rubber particles is 0.2 μm to 0.8 μm.
13. The resin composition according to claim 1 , wherein a rubber content of the graft polymerized rubber particles is 25% by weight to 90% by weight.
14. The resin composition according to claim 1 , wherein a rubber content of the graft polymerized rubber particles is 45% by weight to 80% by weight.
15. The resin composition according to claim 1 , wherein the styrene-acrylonitrile based copolymer is prepared by a solution polymerization method, and the graft polymerized rubber particles are prepared by an emulsion polymerization method.
16. The resin composition according to claim 1 , wherein the resin composition has a mold oil stain weight of less than 0.0055 g as measured by a mold oil stain test.
17. A molded article made of the resin composition according to claim 1 .
18. A food contact container, comprising:
a bottom; and
an outer sidewall, surrounding the bottom;
wherein at least one of the bottom and the outer sidewall comprises the resin composition according to claim 1 .