Method for forming horizontal overhanging structure without vertical support in selective laser melting
A method for forming a horizontal overhanging structure without vertical support in selective laser melting, comprising: sequentially forming an initial layer, a repair layer and a conventional layer, wherein initial layer is printed by scanning at a speed set lower than the conventional speed using a laser spot in a defocused state, so that the Plateau-Rayleigh instability effect occurs in each track, to form an initial layer with a specific texture structure; repair layer is printed on upper surface of the initial layer by scanning at a speed set higher than conventional speed in a continuous-wave laser output mode using a laser spot in a focused state, and completes the transition from transition process parameter to conventional process parameters within the set number of processing layers; and conventional layer is printed on upper surface of repair layer using conventional process parameters, to form a horizontal overhanging structure without vertical support.
1. A method for forming a horizontal overhanging structure in selective laser melting, comprising: sequentially forming an initial layer, a repair layer and a conventional layer, wherein
printing an initial layer by scanning at a speed of V 1 by a laser spot in a defocused state, so that Plateau-Rayleigh instability effect occurs to form the initial layer with a texture structure; wherein a texture direction of the texture structure is different from a scanning direction of the initial layer;
printing a repair layer on an upper surface of the initial layer by scanning at a speed of V 21 in a continuous-wave laser output mode using a laser spot in a focused state; and
printing a conventional layer on an upper surface of the repair layer; wherein the initial layer, the repair layer and the conventional layer form the horizontal overhanging structure;
the repair layer is printed on the upper surface of the initial layer using transition process parameters according to following two phases:
first phase: unidirectionally scanning using continuous-wave laser: wherein
A 21 =A 3 ; V 21 =(3-6) V 3 ; L 3 <L 21 <L 1 ; M 21 =(50%-70%) M 3 ;
wherein:
A 21 represents a diameter of a scanning laser V 21 represents a scanning speed in the first spot in the first phase; phase;
L 21 represents a scanning spacing in the first M 21 represents a linear energy density in the phase; first phase;
a number of the repair layers in the first phase is 2-4, wherein a scanning direction of a first layer of the 2-4 repair layers and the scanning direction of the initial layer form an angle, and scanning directions of subsequent layers of the 2-4 repair layers are rotated 90° layer by layer;
second phase: increasing a line energy density layer by layer; and reducing a scanning spacing layer by layer.
2. The method for forming a horizontal overhanging structure in selective laser melting according to claim 1 , wherein
process parameters of the initial layer are set into:
A 1 =(1.4-1.7) A 3 ; V 1 =(10%-40%) V 3 ; L 1 =(1.3-1.6) L 3 ; M 3 <M 1 ;
where:
A 1 represents a diameter of A 3 represents a diameter of a a scanning laser spot of the scanning laser spot of the conventional layer; initial layer;
V 1 represents a scanning V 3 represents a scanning speed of the speed of the initial layer; conventional layer;
L 1 represents a scanning L 3 represents a scanning spacing of the spacing of the initial layer; conventional layer;
M 1 represents a linear energy M 3 represents a linear energy density of density of the initial layer; the conventional layer;
a number of linear energy density=laser power/scanning the initial layer is 1; speed.
3. The method for forming a horizontal overhanging structure in selective laser melting according to claim 2 , wherein
in the step of printing the initial layer,
continuous-wave laser is used for unidirectionally scanning, wherein a laser power is 40 W, a laser spot diameter is 90-100 μm, the scanning speed of the initial layer is 0.1 m/s, the scanning spacing of the initial layer is 65 μm, a layer thickness is 30 μm; the linear energy density of the initial layer M 1 =400 J/m;
in the step of printing the repair layer,
in the first phase, wherein a laser power is 300 W, a laser spot diameter is 60-70 μm, the scanning speed in the first phase is 1.5 m/s, the scanning spacing in the first phase is 60 μm, a layer thickness is 30 μm; the linear energy density in the first phase M 21 =200 J/m;
in the second phase:
first, pulse laser with a duty ratio of 30% is used for unidirectionally scanning, and an average laser power is gradually increased between 80-90 W, wherein a laser spot diameter is 60-70 μm, a scanning speed is 0.3 m/s, a layer thickness is 30 μm, and a number of repair layers processed is 5; and then, the average laser power is gradually increased between 90-100 W, wherein a scanning spacing is 50 μm, and a number of repair layers processed is 10;
in the step of printing the conventional layer,
pulse laser with a duty ratio of 30% is used for unidirectionally scanning, wherein an average laser power is 100 W, a laser spot diameter is 60-70 μm, the scanning speed of the conventional layer is 0.3 m/s, the scanning spacing of the conventional layer is 50 μm, and a layer thickness is 30 μm; the linear energy density of the conventional layer M 3 =333 J/m.