Multi-metallic catalyst doped with phosphorus and yttrium
The invention relates to a catalyst comprising a support, at least one noble metal M, tin, phosphorus and yttrium, the content of phosphorus element being less than or equal to 1% by weight, and the content of yttrium being less than or equal to 1% by weight relative to the mass of the catalyst. The invention also relates to the process for preparing the catalyst and to the use thereof in reforming.
1. A process for preparing a catalyst wherein the catalyst comprises:
a support,
at least one noble metal M, tin, phosphorus and yttrium,
the phosphorus content being between 0.3% and 1% by weight relative to the mass of the catalyst, and
the yttrium content being less than or equal to 1% by weight relative to the mass of the catalyst, the process comprising the following successive steps:
a) a precursor comprising a support, tin, phosphorus and the noble metal is prepared,
b) the precursor obtained in step a) is dried under a stream of a neutral gas or under a stream of a gas containing oxygen at a temperature below 200° C., and is calcined at a temperature between 350 and 650° C.,
c) the dried and calcined precursor obtained in step b) is impregnated with an impregnation solution comprising an yttrium precursor,
d) the impregnated precursor obtained in step c) is dried under a stream of a neutral gas or under a stream of a gas containing oxygen at a temperature below 200° C., and is calcined at a temperature between 350 and 650° C.
2. Process according to claim 1 , in which step a) comprises the following steps:
a1) a support comprising tin is prepared by introducing a tin precursor during forming of the support,
a2) the support containing tin obtained in step a1) is impregnated with an impregnation solution comprising at least one noble metal precursor and a phosphorus precursor.
3. Process according to claim 1 , in which step a) comprises the following steps:
a1′) a support comprising tin and phosphorus is prepared by introducing a tin precursor and a phosphorus precursor during forming of the support,
a2′) the support containing tin and phosphorus obtained in step a1′) is impregnated with an impregnation solution comprising at least one noble metal precursor.
4. The process according to claim 1 , wherein the catalyst obtained after step d) is subjected to a treatment under hydrogen.