Method of producing three-dimensional object and production apparatus used therefor
A three-dimensional object is obtained by repeating multiple times forming a ceramic powder layer formed of a ceramic powder and applying to a desired region of the ceramic powder layer a liquid precursor composition at least containing at least any one of a metal alkoxide, a metal chloride, a hydrolysate of the metal alkoxide and a polycondensate of the hydrolysate, and water, thereby obtaining a laminated body; subsequently heating the laminated body at a temperature lower than the sintering temperature of the ceramic powder; and removing the ceramic particle in a region to which the precursor composition has not been applied.
1. A method of producing a three-dimensional object through additive manufacturing, comprising:
repeating multiple times forming a ceramic powder layer formed of a ceramic powder and applying to a desired region of the ceramic powder layer a liquid precursor composition at least containing at least one of a metal alkoxide, a metal chloride, a hydrolysate of the metal alkoxide and a polycondensate of the hydrolysate, and water, thereby obtaining a laminated body;
heating the laminated body at a temperature lower than the sintering temperature of the ceramic powder; and
removing the ceramic powder in a region to which the precursor composition has not been applied from the laminated body after the heating.
2. The method of producing a three-dimensional object according to claim 1 , wherein the precursor composition contains an organic solvent.
3. The method of producing a three-dimensional object according to claim 2 , wherein the organic solvent is any of an alcohol, a ketone and a hydrocarbon.
4. The method of producing a three-dimensional object according to claim 1 , wherein the ceramic powder is a metal oxide.
5. The method of producing a three-dimensional object according to claim 1 , wherein the ceramic powder comprises the composition of a ceramic formed from the metal alkoxide.
6. The production method according to claim 1 , wherein the ceramic powder layer is pressurized.
7. The method of producing a three-dimensional object according to claim 1 , wherein the obtained three-dimensional object is heated at a temperature higher than the heating temperature for the laminated body.
8. The method of producing a three-dimensional object according to claim 1 , wherein the method comprises drying the precursor composition applied to the ceramic powder layer, and the temperature at which the laminated body is heated is higher than a temperature at which the precursor composition is dried.
9. The method of producing a three-dimensional object according to claim 1 , wherein the precursor composition is heated to be applied to the ceramic powder layer.
10. The method of producing a three-dimensional object according to claim 1 , wherein a proportion of a ceramic formed from the precursor composition to the precursor composition is 0.1% by mass or more.
11. The method of producing a three-dimensional object according to claim 1 , wherein a solution of a resin is applied to a region of the ceramic powder layer to which the precursor composition has not been applied, the resin being degraded at the temperature at which the laminated body is heated.
12. A production apparatus for producing a three-dimensional object through additive manufacturing, comprising:
a stage on which a three-dimensional object is formed;
a unit forming a ceramic powder layer on the stage;
a unit applying to a desired region of the ceramic powder layer a liquid precursor composition at least containing at least one of a metal alkoxide, a metal chloride, a hydrolysate of the metal alkoxide and a polycondensate of the hydrolysate, and water;
a unit heating a laminated body formed by laminating a plurality of the ceramic powder layers to which the precursor composition has been applied; and
a unit reversibly changing the relative positions of the unit forming the ceramic powder layer and the unit applying the precursor composition with regard to the stage.
13. The production apparatus for a three-dimensional object according to claim 12 , comprising a unit drying the precursor composition at a stage subsequent to the unit applying the precursor composition.
14. The production apparatus for a three-dimensional object according to claim 12 , comprising a unit pressurizing the ceramic powder layer.
15. The production apparatus for a three-dimensional object according to claim 12 , comprising a unit heating the ceramic powder layer at a stage prior to the unit applying the precursor composition.
16. A method of producing a three-dimensional object through additive manufacturing, wherein
forming a precursor composition layer from a liquid precursor composition at least containing at least one of a metal alkoxide, a metal chloride, a hydrolysate of the metal alkoxide and a polycondensate of the hydrolysate, an acidic catalyst promoting hydrolysis of the metal alkoxide, and water, where a proportion of a ceramic formed from the precursor composition to the precursor composition is 1% by mass or more; and
drying the precursor composition layer, thereby forming a ceramic layer are repeated multiple times.
17. The method of producing a three-dimensional object according to claim 16 , wherein the precursor composition contains an organic solvent.
18. The method of producing a three-dimensional object according to claim 17 , wherein the organic solvent is any of an alcohol, a ketone and a hydrocarbon.
19. The method of producing a three-dimensional object according to claim 16 , wherein the acidic catalyst is hydrochloric acid or acetic acid.
20. The method of producing a three-dimensional object according to claim 16 , wherein a thickness of the ceramic layer is 0.05 μm or more and 1 mm or less.
21. The method of producing a three-dimensional object according to claim 16 , wherein the precursor composition contains an inorganic particle.
22. The method of producing a three-dimensional object according to claim 21 , wherein the inorganic particle is a metal oxide.
23. The method of producing a three-dimensional object according to claim 22 , wherein the metal oxide at least contains a metal element contained in the metal alkoxide or metal chloride.
24. The method of producing a three-dimensional object according to claim 16 , wherein the precursor composition is a sol containing a polycondensate formed through hydrolysis and polycondensation reaction of the metal alkoxide.
25. The method of producing a three-dimensional object according to claim 21 , wherein the precursor composition is a sol containing a polycondensate formed through hydrolysis and polycondensation reaction of the metal alkoxide, and a size of the inorganic particle is larger than that of the polycondensate.
26. The method of producing a three-dimensional object according to claim 16 , wherein a solid concentration of the precursor composition is 50% by mass or less.
27. The method of producing a three-dimensional object according to claim 16 , comprising laminating a plurality of the ceramic layers, followed by heating and sintering the ceramic layers.
28. The method of shaping a three-dimensional object according to claim 16 , wherein a three-dimensional object formed of a resin and a ceramic is formed by repeating multiple times forming the ceramic layer in contact with a resin precursor layer or a resin layer.
29. A liquid precursor composition used for additive manufacturing, wherein the precursor composition at least contains at least one of a metal alkoxide, a metal chloride, a hydrolysate of the metal alkoxide and a polycondensate of the hydrolysate, an acidic catalyst promoting hydrolysis of the metal alkoxide, and water, where a proportion of a ceramic formed from the precursor composition to the precursor composition is 1% by mass or more.