Method for the production of a spinning dope composition

1. A method for the production of a spinning dope composition, said method comprising

a homogenization involving vigorous mixing of a cellulosic pulp material in alkali solution, vigorous mixing implying supplying a power density of at least 150 kW/m 3 (kW supplied to agitators per mixed unit of liquid volume) to agitators used in the homogenization, and thereafter

a dissolution involving mixing of the cellulosic pulp material in the alkali solution to obtain a spinning dope composition, wherein the power density supplied to agitators used in the dissolution is maximum 75 kW/m 3 (kW supplied to agitators per mixed unit of liquid volume);

and wherein the cellulosic pulp material in alkali solution is kept at a temperature of less than 0° C. during the homogenization and during at least part of the dissolution.

2. The method according to claim 1 , wherein the power density supplied to agitators used in the homogenization is in a range of 150-4000 kW/m 3 , and wherein the power density supplied to agitators used in the dissolution is maximum 50 kW/m 3 .

3. The method according to claim 1 , wherein the dissolution is performed during a time period sufficient for substantially complete dissolution of cellulose polymers of the cellulosic pulp material in the alkali solution.

4. The method according to claim 1 , wherein the homogenization is performed during a time of less than 120 s.

5. The method according to claim 1 , wherein the dissolution is performed during a time of at least 4 minutes.

6. The method according to claim 1 , wherein the power density supplied to agitators used in the homogenization is in a range of 150-2500 kW/m 3 (kW supplied to agitators per mixed unit of liquid volume).

7. The method according to claim 1 , wherein the power density supplied to agitators used in the dissolution is in a range of 2-50 kW/m 3 .

8. The method according to claim 1 , wherein:

a product of power density * residence time is in a range of 4000-20000 (kW*s)/m 3 , in a power density range of 200-2000 kW/m 3 , and for residence times in a range of 1-30 seconds in the homogenization; and

the product of power density * residence time is in a range of 4000-25000 (kW*s)/m 3 in a power density range of 4-50 kW/m 3 and for residence times in a range of 240-1800 seconds in the dissolution.

9. The method according to claim 1 , wherein temperature in the cellulosic pulp material in alkali solution is held within a range of from −8 to −3° C. during the homogenization and during at least part of the dissolution.

10. The method according to claim 1 , wherein the vigorous mixing in the homogenization involves high shear mixing with a rotation speed of at least 1000 rpm.

11. The method according to claim 1 , wherein the mixing in the dissolution is performed with a rotation speed below 300 rpm.

12. The method according to claim 1 , wherein the cellulosic pulp material being processed is a non-derivatised or low-derivatised cellulose pulp.

13. The method according to claim 1 , wherein the method also comprises at least one refining performed subsequent to the dissolution, said refining providing viscous dissipation and a temperature increase to the spinning dope composition by shearing.

14. The method according to claim 13 , wherein the temperature increase in the refining is 0.2-10° C.

15. The method according to claim 13 , wherein the refining is performed with a power density in a range of 1000-8000 kW/m 3 .

16. The method according to claim 13 , wherein the refining is performed with a power density in a range of 2000-6000 kW/m 3 .

17. The method according to claim 13 , wherein a product of power density * residence time is in a range of 2000-15000 (kW*s)/m 3 in a power density range of 1000-6000 kW/m 3 , and for residence times in a range of 0.5-5 seconds in the refining.

18. The method according to claim 13 , wherein at least one further dissolution is performed subsequent to at least one of said at least one refining.

19. The method according to claim 1 , wherein the cellulosic pulp material is pre-treated prior to homogenization by shortening chains of cellulose polymers by cleavage of cellulose chains.

20. The method according to claim 19 , wherein the shortening of the chains of cellulose polymers is performed at least partly by wet grinding in alkali solution.

21. The method according to claim 19 , wherein the shortening of the chains of cellulose polymers is performed at least partly by a method selected among: hydrolysis with sulfuric acid, steam explosion treatment, hydrothermal or treatment.

22. The method according to claim 1 , wherein the alkali solution comprises sodium hydroxide in a concentration range of 7-8 wt % calculated on a total weight of the spinning dope composition.

23. The method according to claim 22 , wherein the concentration of sodium hydroxide is in a range of 7.2-7.8 wt % calculated on the total weight of the spinning dope composition.

24. The method according to claim 1 , wherein a concentration of the cellulosic pulp material is in a range of 5-12 wt % calculated on a total weight of the spinning dope composition.

25. The method according to claim 1 , wherein an additive for gelation prevention is added so that the additive is present during the homogenization.

26. The method according to claim 25 , wherein the additive for gelation prevention is ZnO added in a concentration range of 0.5-1.4 wt % calculated on a total weight of the spinning dope composition.

27. The method according to claim 1 , wherein the method involving homogenization and dissolution is performed continuously.

28. The method according to claim 1 , wherein the dissolution is finalized by passing the cellulosic material in the alkali solution through a mechanical working step in which high shear forces are applied to increase a temperature of the spinning dope composition to a point within a range of from 0 to 30° C.

29. The method according to claim 1 , said method also involving a subsequent treatment of the spinning dope composition in a coagulation bath.

30. The method according to claim 1 , wherein the homogenization is performed according to a plug flow principle and the dissolution is performed according to a continuous stirred tank reactor principle.

31. The method according to claim 4 , wherein the homogenization is performed during a time of less than 60 s.

32. The method according to claim 1 , wherein the power density supplied to agitators used in the homogenization is at least a factor 5 higher than the power density supplied to agitators used in the dissolution.

33. The method according to claim 1 , wherein a time for performing the dissolution is at least a factor 5 longer than a time for performing the homogenization.

34. The method according to claim 5 , wherein the dissolution is performed during a time of 5-60 minutes.

35. The method according to claim 25 , wherein said additive is urea or comprising zinc.

36. The method according to claim 29 , wherein said coagulation bath comprises sodium carbonate or sodium sulfate.