Negative electrode for non-aqueous electrolyte secondary battery
A negative electrode for non-aqueous electrolyte secondary battery provides a means for improving output characteristics at a high rate. The negative electrode has a negative electrode active material layer having a thickness of 150 to 1500 μm formed on a surface of a current collector. In addition, the negative electrode active material layer includes coated negative electrode active material particles in which at least a part of a surface of a negative electrode active material is coated with a coating agent containing a coating resin and a conductive aid. Furthermore, a porosity of the negative electrode active material layer is 39.0% to 60.0% and a density of the negative electrode active material layer is 0.60 to 1.20 g/cm 3 .
1. A negative electrode for non-aqueous electrolyte secondary battery having a negative electrode active material layer having a thickness of 150 to 1500 μm formed on a surface of a current collector, wherein
the negative electrode active material layer includes coated negative electrode active material particles in which at least a part of a surface of a negative electrode active material is coated with a coating agent containing a coating resin and a conductive aid,
a porosity of the negative electrode active material layer is 39.0% to 45.6% and a density of the negative electrode active material layer is 0.80 g/cm 3 to 0.91 g/cm 3 , and
the coated negative electrode active material particles have a core-shell structure in which a shell portion made of the coating agent containing the coating resin and the conductive aid is formed on the surface of a core portion made of the negative electrode active material.
2. The negative electrode for non-aqueous electrolyte secondary battery according to claim 1 , wherein a porosity of the negative electrode active material layer is 40.8% or more and 45.6% or less.
3. The negative electrode for non-aqueous electrolyte secondary battery according to claim 1 , wherein a tensile elongation at break of the coating resin is 10% or more in a saturated liquid absorbing state.
4. The negative electrode for non-aqueous electrolyte secondary battery according to claim 1 , wherein a content of a binder in the negative electrode active material layer is 1% by mass or less with respect to a total solid content of 100% by mass.
5. The negative electrode for non-aqueous electrolyte secondary battery according to claim 1 , wherein the coating resin is at least one selected from the group consisting of a polyurethane resin and a polyvinyl-based resin.
6. The negative electrode for non-aqueous electrolyte secondary battery according to claim 1 , wherein a content of a binder in the negative electrode active material layer is 0.1% by mass or less with respect to a total solid content of 100% by mass.
7. The negative electrode for non-aqueous electrolyte secondary battery according to claim 1 , wherein a content of a binder in the negative electrode active material layer is 0% by mass with respect to a total solid content of 100% by mass.
8. A non-aqueous electrolyte secondary battery comprising a power generating element including:
the negative electrode for non-aqueous electrolyte secondary battery according to claim 1 ;
a positive electrode having a positive electrode active material layer including a positive electrode active material formed on a surface of a current collector; and
an electrolytic layer disposed between the negative electrode and the positive electrode.
9. The non-aqueous electrolyte secondary battery according to claim 8 , wherein
the negative electrode active material layer further includes a conductive member,
at least a part of the conductive member forms a conductive path for electrically connecting a first main surface in contact with the electrolytic layer side of the negative electrode active material layer to a second main surface in contact with the current collector side, and
the conductive path and the negative electrode active material are electrically connected to each other.