UV curable inkjet inks
A liquid UV curable inkjet ink includes one or more photoinitiators, an organic colour pigment, and a polymerizable composition containing at least one monofunctional polymerizable compound and at least one polyfunctional polymerizable compound, wherein the organic colour pigment is present in an amount of 6.0 to 13.0 wt % based on the total weight of the liquid UV curable inkjet ink; the at least one polyfunctional polymerizable compound is present in an amount of at least 20.0 wt % based on the total weight of the polymerizable composition; and the UV curable inkjet ink has a viscosity at 45° C. and a shear rate of 10 s−1 of at least 16.0 mPa.s.
1. A liquid UV curable inkjet ink comprising:
one or more photoinitiators in an amount of at least 7.0 wt % relative to a total weight of the liquid UV curable inkjet ink;
an organic color pigment; and
a polymerizable composition in an amount less than 75 wt % relative to the total weight of the liquid UV curable inkjet ink and including at least one monofunctional polymerizable compound and at least one polyfunctional polymerizable compound; wherein
the organic color pigment is present in an amount of 6.0 to 13.0 wt % based on the total weight of the liquid UV curable inkjet ink;
the at least one polyfunctional polymerizable compound is present in an amount of 20.0 wt % to 50.0 wt % based on a total weight of the polymerizable composition;
the liquid UV curable inkjet ink has a viscosity at 45° C. and a shear rate of 10 s −1 of at least 16.0 mPa.s; and
the liquid UV curable inkjet ink has a viscosity at 25° C. and a shear rate of 10 s −1 of at least 40.0 mPa.s.
2. The liquid UV curable inkjet ink according to claim 1 , wherein the at least one polyfunctional polymerizable compound is present in an amount of 25.0 to 50.0 wt % based on the total weight of the polymerizable composition.
3. The liquid UV curable inkjet ink according to claim 1 , wherein at least one of the one or more photoinitiators is selected from the group consisting of a polymeric photoinitiator, a polymerizable photoinitiator, and a photoinitiator including a plurality of photoinitiating groups.
4. The liquid UV curable inkjet ink according to claim 1 , wherein the polymerizable composition is present in amount less than 70.0 wt % based on the total weight of the liquid UV curable inkjet ink.
5. The liquid UV curable inkjet ink according to claim 1 , further comprising 0 to 10 wt % of an organic solvent based on the total weight of the liquid UV curable inkjet ink.
6. The liquid UV curable inkjet ink according to claim 1 , wherein the viscosity is from 20.0 to 65.0 mPa.s at 45° C. and a shear rate of 10 s −1 .
7. The liquid UV curable inkjet ink according to claim 1 , wherein the one or more photoinitiators includes an acylphosphine oxide photoinitiator and a thioxanthone photoinitiator.
8. A UV curable inkjet ink set for printing different colors comprising:
at least one liquid UV curable inkjet ink according to claim 1 .
9. The UV curable inkjet ink set according to claim 8 , wherein
the UV curable inkjet ink set includes at least three liquid UV curable color inkjet inks, each including one or more different organic color pigments present in an amount of 6.0 to 13.0 wt % based on the total weight of the liquid UV curable color inkjet ink.
10. The UV curable inkjet ink set according to claim 8 , further comprising:
a liquid UV curable white inkjet ink including a titanium dioxide pigment having an average particle size larger than 180 nm.
11. The UV curable inkjet ink set according to claim 8 , further comprising:
a liquid UV curable black ink including a carbon black pigment and a β-copper phthalocyanine pigment having an average particle size smaller than 200 nm.
12. A UV curable inkjet printing method comprising the steps of:
jetting at least one liquid UV curable inkjet ink according to claim 1 onto a substrate with a print head at a jetting temperature of 45° C. or more; and
UV curing the at least one liquid UV curable inkjet ink jetted on the substrate.
13. The UV curable inkjet printing method according to claim 12 , wherein the substrate is pre-treated by a corona, a plasma, or a flame treatment.
14. The UV curable inkjet printing method according to claim 12 , wherein the print head is a through-flow piezoelectric drop-on-demand print head.
15. The UV curable inkjet printing method according to claim 12 , wherein the at least one liquid UV curable inkjet ink is jetted at a temperature between 45° C. and 65° C.