Dielectric ceramic composition and multilayer ceramic electronic component having the same

Inventors: Seok Hyun Yoon (Suwon-si, KR); Chan Hee Nam (Suwon-si, KR); Song Je Jeon (Suwon-si, KR); Chang Hak Choi (Suwon-si, KR)

Assignee: SAMSUNG ELECTRO-MECHANICS CO., LTD.

H01G4/1227 H01G4/30

View Patent ↗

Loading inventors, assignments & file history…

Monitor This Case

Get email alerts when status or documents change.

Order Certified Copies

Most orders are placed with the USPTO same day — all within 24 business hours.

Order via The Patent Place →

Pre-filled with this patent's details

Quick Facts

Patent No.: US 11,309,129
App. No.: 16/777,182
Granted: Apr 19, 2022
Kind: B2

External Links

USPTO Patent Center↗ Full Patent PDF↗

Abstract

A dielectric ceramic composition includes a base material main component of barium titanate and a subcomponent. A microstructure of the dielectric ceramic composition after sintering includes a first grain having a Ca content of less than 3.5 at % and a second grain having a Ca content of 3.5 to 13.5 at %, and an area ratio of the second grain to an area of the total grains is 70% to 95%.

Claims (112)

1. A dielectric ceramic composition comprising:

a base material main component of barium titanate and a subcomponent,

wherein a microstructure of the dielectric ceramic composition after sintering includes a first grain having a Ca content of less than 3.5 at % and a second grain having a Ca content of 3.5 to 13.5 at %,

wherein an area ratio of the second grain to an area of a sum of the first and second grains is 70% to 95%,

wherein the base material main component comprises a first base material main component represented by (Ba 1−x Ca x )TiO 3 (x≤0.035) and a second base material main component represented by (Ba 1−y Ca y )TiO 3 (0.035≤y≤0.135), and

wherein a molar ratio of the first base material main component to the second base material main component is (1−z):z, in which 0.9≤z≤0.95.

2. The dielectric ceramic composition of claim 1 , wherein the subcomponent comprises at least one of:

a first subcomponent comprising at least one selected from the group consisting of a variable-valence acceptor element including at least one of manganese (Mn), vanadium (V), chromium (Cr), iron (Fe), nickel (Ni), cobalt (Co), copper (Cu), and zinc (Zn), oxides thereof, or carbonates thereof;

a second subcomponent comprising at least one of fixed-valence acceptor elements including Mg, oxides thereof, or carbonates thereof;

a third subcomponent comprising at least one selected from the group consisting of at least one of yttrium (Y), dysprosium (Dy), holmium (Ho), erbium (Er), gadolinium (Gd), cerium (Ce), neodymium (Nd), samarium (Sm), terbium (Tb), thulium (Tm), lanthanum (La) and ytterbium (Yb), oxides thereof, or carbonates thereof;

a fourth subcomponent comprising at least one selected from the group consisting of at least one of barium (Ba) and calcium (Ca), oxides thereof, or carbonates thereof; and

a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a silicon (Si) element, a carbonate of a Si element, and a glass containing a Si element.

3. The dielectric ceramic composition of claim 2 , wherein a sum of contents of variable-valence acceptor elements of one or more of Mn, V, Cr, Fe, Ni, Co, Cu and Zn included in the first subcomponent is 0.1 to 2.0 mole parts based on 100 mole parts of the base material main component,

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component,

a sum of contents of one or more of Y, Dy, Ho, Er, Gd, Ce, Nd, Sm, Tb, Tm, La and Yb included in the third subcomponent is 2.0 to 7 mole parts based on 100 mole parts of the base material main component,

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component, and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

4. The dielectric ceramic composition of claim 1 , wherein the subcomponent comprises a first subcomponent comprising at least one selected from the group consisting of variable-valence acceptor elements comprising at least one of Mn, V, Cr, Fe, Ni, Co, Cu and Zn, oxides thereof, or carbonates thereof; and

a sum of contents of variable-valence acceptor elements of one or more of Mn, V, Cr, Fe, Ni, Co, Cu and Zn included in the first subcomponent is 0.1 to 2.0 mole parts based on 100 mole parts of the base material main component.

5. The dielectric ceramic composition of claim 1 , wherein the subcomponent comprises a second subcomponent comprising at least one of fixed-valence acceptor elements comprising Mg, oxides thereof, or carbonates thereof; and

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

6. The dielectric ceramic composition of claim 1 , wherein the subcomponent comprises a third subcomponent comprising at least one selected from the group consisting of at least one of Y, Dy, Ho, Er, Gd, Ce, Nd, Sm, Tb, Tm, La and Yb, oxides thereof, or carbonates thereof; and

7. The dielectric ceramic composition of claim 1 , wherein the subcomponent comprises a fourth subcomponent comprising at least one selected from the group consisting of at least one of Ba and Ca, oxides thereof, or carbonates thereof; and

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

8. The dielectric ceramic composition of claim 1 , wherein the subcomponent comprises a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a Si element, a carbonate of a Si element, and a glass containing a Si element; and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

9. A multilayer ceramic electronic component comprising:

a ceramic body including a dielectric layer and an internal electrode; and

an external electrode disposed on an external surface of the ceramic body and electrically connected to the internal electrode,

wherein a microstructure of the dielectric layer includes a first grain having a Ca content of less than 3.5 at % and a second grain having a Ca content of 3.5 to 13.5 at %,

wherein an area ratio of the second grain to an area of a sum of the first and second grains is 70% to 95%,

wherein the dielectric layer comprises a dielectric ceramic composition comprising a base material main component of barium titanate and a subcomponent,

wherein the base material main component includes a first base material main component represented by (Ba 1−x Ca x )TiO 3 (x≤0.035) and a second base material main component represented by (Ba 1−y Ca y )TiO 3 (0.035≤y≤0.135), and

wherein a molar ratio of the first base material main component to the second base material main component is (−z):z, in which 0.9≤z≤0.95.

10. The multilayer ceramic electronic component of claim 9 , wherein the subcomponent comprises at least one of:

a second subcomponent comprising at least one of fixed-valence acceptor elements including Mg, oxides thereof, and carbonates thereof;

a fourth subcomponent comprising at least one selected from the group consisting of at least one of barium (Ba) and calcium (Ca), oxides thereof, or carbonates thereof; and

a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a silicon (Si) element, a carbonate of a Si element, and a glass containing a Si element.

11. The multilayer ceramic electronic component of claim 10 , wherein a sum of contents of variable-valence acceptor elements of one or more of Mn, V, Cr, Fe, Ni, Co, Cu and Zn included in the first subcomponent is 0.1 to 2.0 mole parts based on 100 mole parts of the base material main component,

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component,

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component, and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

12. The multilayer ceramic electronic component of claim 9 , wherein the subcomponent comprises a first subcomponent comprising at least one selected from the group consisting of variable-valence acceptor elements comprising at least one of Mn, V, Cr, Fe, Ni, Co, Cu and Zn, oxides thereof, or carbonates thereof; and

13. The multilayer ceramic electronic component of claim 9 , wherein the subcomponent comprises a second subcomponent comprising at least one of fixed-valence acceptor elements comprising Mg, oxides thereof, or carbonates thereof; and

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

14. The multilayer ceramic electronic component of claim 9 , wherein the subcomponent comprises a third subcomponent comprising at least one selected from the group consisting of at least one of Y, Dy, Ho, Er, Gd, Ce, Nd, Sm, Tb, Tm, La and Yb, oxides thereof, or carbonates thereof; and

15. The multilayer ceramic electronic component of claim 9 , wherein the subcomponent comprises a fourth subcomponent comprising at least one selected from the group consisting of at least one of Ba and Ca, oxides thereof, or carbonates thereof; and

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

16. The multilayer ceramic electronic component of claim 9 , wherein the subcomponent comprises a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a Si element, a carbonate of a Si element, and a glass containing a Si element; and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

17. A dielectric ceramic composition comprising:

a base material main component of barium titanate and a subcomponent,

wherein an area ratio of the second grain to an area of a sum of the first and second grains is 70% to 95%,

wherein the base material main component excludes CaZrO 3 and comprises a first base material main component represented by (Ba 1−x Ca x )TiO 3 (x≤0.035) and a second base material main component represented by (Ba 1−y Ca y )TiO 3 (0.035≤y≤0.135), and

wherein a molar ratio of the first base material main component to the second base material main component is (1−z):z, in which 0.7≤z≤0.95.

18. A multilayer ceramic electronic component comprising:

a ceramic body including a dielectric layer and an internal electrode; and

an external electrode disposed on an external surface of the ceramic body and electrically connected to the internal electrode,

wherein a microstructure of the dielectric layer includes a first grain having a Ca content of less than 3.5 at % and a second grain having a Ca content of 3.5 to 13.5 at %,

wherein an area ratio of the second grain to an area of a sum of the first and second grains is 70% to 95%,

wherein the dielectric layer comprises a dielectric ceramic composition comprising a base material main component of barium titanate and a subcomponent,

wherein the base material main component excludes CaZrO 3 and includes a first base material main component represented by (Ba 1−x Ca x )TiO 3 (x≤0.035) and a second base material main component represented by (Ba 1−y Ca y )TiO 3 (0.035≤y≤0.135), and

wherein a molar ratio of the first base material main component to the second base material main component is (1−z):z, in which 0.7≤z≤0.95.

19. The dielectric ceramic composition of claim 17 , wherein the subcomponent comprises at least one of:

a second subcomponent comprising at least one of fixed-valence acceptor elements including Mg, oxides thereof, or carbonates thereof;

a fourth subcomponent comprising at least one selected from the group consisting of at least one of barium (Ba) and calcium (Ca), oxides thereof, or carbonates thereof; and

a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a silicon (Si) element, a carbonate of a Si element, and a glass containing a Si element.

20. The dielectric ceramic composition of claim 19 , wherein a sum of contents of variable-valence acceptor elements of one or more of Mn, V, Cr, Fe, Ni, Co, Cu and Zn included in the first subcomponent is 0.1 to 2.0 mole parts based on 100 mole parts of the base material main component,

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component,

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component, and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

21. The dielectric ceramic composition of claim 17 , wherein the subcomponent comprises a first subcomponent comprising at least one selected from the group consisting of variable-valence acceptor elements comprising at least one of Mn, V, Cr, Fe, Ni, Co, Cu and Zn, oxides thereof, or carbonates thereof; and

22. The dielectric ceramic composition of claim 17 , wherein the subcomponent comprises a second subcomponent comprising at least one of fixed-valence acceptor elements comprising Mg, oxides thereof, or carbonates thereof; and

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

23. The dielectric ceramic composition of claim 17 , wherein the subcomponent comprises a third subcomponent comprising at least one selected from the group consisting of at least one of Y, Dy, Ho, Er, Gd, Ce, Nd, Sm, Tb, Tm, La and Yb, oxides thereof, or carbonates thereof; and

24. The dielectric ceramic composition of claim 17 , wherein the subcomponent comprises a fourth subcomponent comprising at least one selected from the group consisting of at least one of Ba and Ca, oxides thereof, or carbonates thereof; and

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

25. The dielectric ceramic composition of claim 17 , wherein the subcomponent comprises a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a Si element, a carbonate of a Si element, and a glass containing a Si element; and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

26. The multilayer ceramic electronic component of claim 18 , wherein the subcomponent comprises at least one of:

a second subcomponent comprising at least one of fixed-valence acceptor elements including Mg, oxides thereof, and carbonates thereof;

a fourth subcomponent comprising at least one selected from the group consisting of at least one of barium (Ba) and calcium (Ca), oxides thereof, or carbonates thereof; and

a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a silicon (Si) element, a carbonate of a Si element, and a glass containing a Si element.

27. The multilayer ceramic electronic component of claim 26 , wherein a sum of contents of variable-valence acceptor elements of one or more of Mn, V, Cr, Fe, Ni, Co, Cu and Zn included in the first subcomponent is 0.1 to 2.0 mole parts based on 100 mole parts of the base material main component,

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component,

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component, and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

28. The multilayer ceramic electronic component of claim 18 , wherein the subcomponent comprises a first subcomponent comprising at least one selected from the group consisting of variable-valence acceptor elements comprising at least one of Mn, V, Cr, Fe, Ni, Co, Cu and Zn, oxides thereof, or carbonates thereof; and

29. The multilayer ceramic electronic component of claim 18 , wherein the subcomponent comprises a second subcomponent comprising at least one of fixed-valence acceptor elements comprising Mg, oxides thereof, or carbonates thereof; and

the content of the fixed-valence acceptor elements including Mg, included in the second subcomponent, is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

30. The multilayer ceramic electronic component of claim 18 , wherein the subcomponent comprises a third subcomponent comprising at least one selected from the group consisting of at least one of Y, Dy, Ho, Er, Gd, Ce, Nd, Sm, Tb, Tm, La and Yb, oxides thereof, or carbonates thereof; and

31. The multilayer ceramic electronic component of claim 18 , wherein the subcomponent comprises a fourth subcomponent comprising at least one selected from the group consisting of at least one of Ba and Ca, oxides thereof, or carbonates thereof; and

a sum of contents of one or more of Ba and Ca included in the fourth subcomponent is 0.5 to 3.0 mole parts based on 100 mole parts of the base material main component.

32. The multilayer ceramic electronic component of claim 18 , wherein the subcomponent comprises a fifth subcomponent comprising at least one selected from the group consisting of an oxide of a Si element, a carbonate of a Si element, and a glass containing a Si element; and

a content of the Si element included in the fifth subcomponent is 0.5 to 4.0 mole parts based on 100 mole parts of the base material main component.

Assignments (1)

ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Jan 30, 2020

From: YOON, SEOK HYUN; NAM, CHAN HEE; JEON, SONG JE; CHOI, CHANG HAK

To: SAMSUNG ELECTRO-MECHANICS CO., LTD.

Reel/Frame 051761/0479 →

Priority Claims (2)

KR 10-2019-0078009 · Jun 28, 2019 · national

KR 10-2019-0094914 · Aug 5, 2019 · national

Continuity (1)

Related Publication 20200411239A1 · Dec 31, 2020