Processes for making weather resistant, slow-decaying, durable natural fiber/coir geotextiles produce geotextiles having flexibility, permeability, light weight and cost-effective characteristics. In this process an in situ chemical grafting using a mixture of Cashew Nut Shell Liquid and aminoalkyl trialkoxysilanes with cellulose was done followed by curing in presence of sunlight, UV light or heat. The developed product showed durability and strength more than that of natural fiber/fabric and retaining natural fiber/fabric/geotextiles characteristics. The geotextiles have delayed bio-deterioration having wider long-term end use/applications. This process of making durable geotextiles is eco-friendly and retains the desired characteristic.
1. A process for preparing a functionalized weather-resistant and slow-decaying geotextile fabric formed of coir fibers, the process comprising:
(a) mixing 3-pentadecenyl phenols with aminoalkyl trialkoxysilanes in a ratio of from 1:1 to 3:1 (v/v) at a temperature of 30° C.±5° C. and humidity of 60% to 70% to obtain a mixture;
(b) impregnating or coating the coir fibers of the geotextile fabric with the mixture as obtained in (a); and
(c) curing the impregnated or coated coir fibers obtained in (b) under heat, UV, air, or sunlight to obtain the functionalized weather-resistant and slow-decaying geotextile fabric.
2. The process of claim 1 , wherein the coir fibers are from Cocos nucifera and are in woven or non-woven form.
3. The process of claim 1 , wherein the 3-pentadecenyl phenols are selected from the group consisting of cashew nut shell liquid, urushiol, cardanol, cardol, and anacardic acid.
4. The process of claim 1 , wherein the aminoalkyl trialkoxysilanes are selected from the group consisting of aminopropyl triethoxysilane and 2-aminoethyl triethoxysilane.
5. The process of claim 1 , wherein curing the impregnated or coated coir fibers comprises keeping the coir fibers at a temperature of 30° C.±5° C. and at a humidity of 60% to 70% for 3 days to 7 days.
6. The process of claim 1 , wherein curing the impregnated or coated coir fibers comprises keeping the coir fibers in sunlight for a period of 6 hours to 12 hours, or in UV-light for a period of 3 hours to 5 hours, or in an air oven at a temperature from 60° C. to 90° C. for a period of 5 hours to 8 hours.
7. The process of claim 1 , wherein curing the impregnated coir fibers comprises keeping the coir fibers at a temperature of 30° C.±5° C. for a period of 7 days to 10 days.
8. The process of claim 1 , wherein (a) further comprises keeping the mixture at a temperature of 30° C.±5° C. at a humidity of 60% to 65% for 7 days to 10 days, and wherein (b) comprises coating the coir fibers of the geotextile fabric in the presence of 2% to 5% of excess 3-aminopropyl trimethoxysilane, and wherein (c) comprises curing the coated coir fibers for a period of 0.5 hours to 1.0 hours under UV light.