Layered polyester film
To provide a layered polyester film having excellent mechanical properties, transparency, heat resistance, and in particular excellent gas barrier property. A layered polyester film containing a polyester film and a thin film layer including mainly an inorganic compound, wherein the polyester film is a biaxially oriented polyester film including a dicarboxylic acid component containing mainly a furandicarboxylic acid and a glycol component containing mainly ethylene glycol, the thin film layer is formed on at least one surface of the polyester film, the inorganic compound is at least one of aluminum oxide and silicon oxide, and the layered polyester film has a plane orientation coefficient ΔP of not less than 0.100 and not more than 0.200, a film thickness of not thinner than 1 μm and not thicker than 300 μm, and an oxygen permeability of not less than 0.1 mL/m 2 /day/MPa and not more than 80 mL/m 2 /day/MPa under a temperature of 23° C. and a humidity of 65%.
1. A layered polyester film comprising a polyester film and an inorganic compound layer including mainly an inorganic compound, wherein
the polyester film is a biaxially oriented polyester film including a dicarboxylic acid component containing mainly a furandicarboxylic acid and a glycol component containing mainly ethylene glycol,
the inorganic compound layer is formed on at least one surface of the polyester film,
the inorganic compound is at least one of aluminum oxide and silicon oxide, and
the layered polyester film has a plane orientation coefficient ΔP of not less than 0.100 and not more than 0.200, a film thickness of not thinner than 1 μm and not thicker than 300 μm, and an oxygen permeability of not less than 0.1 mL/m 2 /day/MPa and not more than 80 mL/m 2 /day/MPa under a temperature of 23° C. and a humidity of 65%.
2. The layered polyester film according to claim 1 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 30% when heated at 150° C. for 30 minutes.
3. The layered polyester film according to claim 1 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 20% when heated at 150° C. for 30 minutes.
4. The layered polyester film according to claim 1 , wherein the polyester film has a heat shrinkage rate of not less than 0.01% and not more than 10% when heated at 150° C. for 30 minutes.