Method for producing high-pressure tank
A method for producing a high-pressure tank capable of suppressing break of a surface resin layer due to gas pressure as well as degradation in the tank quality. The method includes winding a thermosetting resin-impregnated fiber bundle around a liner so as to form an uncured fiber-reinforced resin layer thereon, first heating in which the uncured fiber-reinforced resin layer is locally heated at a first temperature so as to leach the thermosetting resin out of the uncured fiber-reinforced resin layer to form the surface resin layer, and the surface resin layer is cured to have cracks generated therein, and second heating in which the tank is entirely heated at a second temperature lower than the first temperature, so that the fiber-reinforced resin layer and surface resin layer are entirely cured, so as to obtain the tank with the surface resin layer locally having cracks generated therein.
1. A method for producing a high-pressure tank including a resin liner, a fiber-reinforced resin layer covering an outer surface of the liner, and a surface resin layer covering an outer surface of the fiber-reinforced resin layer, the method comprising:
winding a thermosetting resin-impregnated fiber bundle around the outer surface of the liner so as to form an uncured fiber-reinforced resin layer on the outer surface of the liner;
a first heating operation in which a region of the uncured fiber-reinforced resin layer is locally heated at a first temperature, such that a portion of the thermosetting resin leaches out of said region of the uncured fiber-reinforced resin layer so as to form the surface resin layer, wherein the surface resin layer is cured;
cooling the heated and cured surface resin layer to a second temperature that is lower than the first temperature, such that cracks are generated in the surface resin layer; and
a second and subsequent heating operation in which the high-pressure tank is entirely heated at a third temperature that is lower than the first temperature and higher than the second temperature, such that the fiber-reinforced resin layer is cured, so as to obtain the high-pressure tank with the surface resin layer having said cracks.
2. The method for producing a high-pressure tank according to claim 1 , wherein the region that is locally heated in the first heating operation includes an end of the fiber bundle that is wound.
3. The method for producing a high-pressure tank according to claim 1 , wherein the first heating operation includes heating the uncured fiber-reinforced resin layer by locally blowing hot air to the uncured fiber-reinforced resin layer.