Method for producing hot forged material
Provided is a method for producing a hot forged material capable of preventing the generation of double-barreling shaped forging defects. The method for producing a hot forged material, wherein both an upper die and a lower die are made of Ni-based super heat-resistant alloy and the method comprises a hot forging step of pressing a material for hot forging by the lower die and the upper die in the air to form the hot forged material, the method comprising: a raw material heating step of heating the material for hot forging in a furnace to a heating temperature within a range of 1025 to 1150° C.; a die heating step of heating the upper die and the lower die to a heating temperature within a range of 950 to 1075° C.; and a transferring step of transferring the material for hot forging onto the lower die by a manipulator after the completion of the raw material heating step and the die heating step, wherein a value obtained by subtracting the heating temperature of the upper die and the lower die from the heating temperature of the material for hot forging is 75° C. or more.
1. A method for producing a hot forged material, wherein both an upper die and a lower die are made of Ni-based super heat-resistant alloy, the method comprising:
a raw material heating step of heating the material for hot forging in a furnace to a heating temperature within a range of 1025 to 1150° C.;
a die heating step of heating the upper die and the lower die to a heating temperature within a range of 1000 to 1075° C.; and
a transferring step of transferring the material for hot forging onto the lower die by a manipulator after the completion of the raw material heating step and the die heating step; and
a hot die forging step of pressing the material for hot forging by the lower die and the upper die in air to form the hot forged material,
wherein a value obtained by subtracting the heating temperature of the upper die and the lower die from the heating temperature of the material for hot forging is 75° C. or more, and
the lower die and the upper die have a high-temperature compressive strength of 300 MPa or more under conditions of a strain rate of 10 −3 /sec at 1100° C.
2. The method for producing a hot forged material according to claim 1 , wherein the Ni-based super heat-resistant alloy has a composition comprising, in mass %, W: 7.0 to 15.0%, Mo: 2.5 to 11.0%, and Al: 5.0 to 7.5%; as selective elements, Cr: 7.5% or less, Ta: 7.0% or less, Ti: 7.0% or less, Nb: 7.0% or less, Co: 15.0% or less, C: 0.25% or less, B: 0.05% or less, Zr: 0.5% or less, Hf: 0.5% or less, rare-earth elements: 0.2% or less, Y: 0.2% or less, and Mg: 0.03% or less; and the balance being Ni and inevitable impurities.
3. A method for producing a hot forged material according to claim 1 , wherein before the material for hot forging is heated in the furnace to the heating temperature, a lubricating coating is provided on a surface of the material for hot forging by application of a liquid lubricant.
4. The method for producing a hot forged material according to claim 1 , wherein the Ni-based super heat-resistant alloy has a composition comprising, in mass %, W: 7.0 to 15.0%, Mo: 2.5 to 11.0%, Al: 5.0 to 7.5%, and Cr: 0.5 to 7.5%; as selective elements, Ta: 7.0% or less, Ti: 7.0% or less, Nb: 7.0% or less, Co: 15.0% or less, C: 0.25% or less, B: 0.05% or less, Zr: 0.5% or less, Hf: 0.5% or less, rare-earth elements: 0.2% or less, Y: 0.2% or less, and Mg: 0.03% or less; and the balance being Ni and inevitable impurities.