Light-tight shrink wrapping film
The invention relates to a heat-shrinkable film comprising a first polymer ply A comprising at least one dark pigment, a second polymer ply B comprising at least one white pigment, wherein the thickness ratio of the first ply A is in the range of 5:95 to 50:50, the film has a thickness of 20 μm bis 100 μm, the light transmission of the film is not more than 12%, and the film after 15 seconds in a water bath having a temperature of 95° C. exhibits shrinkage in a main shrinking direction in the range of 20% to 85%. The invention further relates to a hose comprising such a heat-shrinkable film and to a process for producing such a heat-shrinkable film.
1. Heat-shrinkable, uniaxially stretched film consisting of:
a first polymer ply A which comprises at least one dark pigment;
a second polymer ply B which comprises at least one white pigment; and
at least one pigment ply consisting of pigments applied to the second polymer ply B,
wherein:
the first polymer ply A and the second polymer ply B, independently of each other, comprise one or more polymers which are selected from the group of the polyesters, polyolefins, polystyrenes and polyvinyl halides,
the film has a thickness of 20 μm to 100 μm,
the thickness ratio of the first polymer ply A to the second polymer ply B is in the range 5:95 to 50:50,
the light transmission of the film is not more than 12%, and
the film after 15 seconds in a water bath having a temperature of 95° C. exhibits shrinkage in a main shrinking direction in the range of 20% to 85%.
2. Heat-shrinkable film according to claim 1 , wherein the second polymer ply B has an L* value of at least 85.
3. Heat-shrinkable film according to claim 1 , wherein at least one of the surfaces which face away from each other of the first polymer ply A and of the second polymer ply B is smooth.
4. Heat-shrinkable film according to claim 1 , wherein the second polymer ply B can be printed on.
5. Heat-shrinkable film according to claim 1 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polyester.
6. Heat-shrinkable film according to claim 1 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polyolefin.
7. Heat-shrinkable film according to claim 1 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polystyrene.
8. Heat-shrinkable film according to claim 1 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polyvinyl halide.
9. Heat shrinkable film according to claim 1 , wherein the second polymer ply B has a roughness Rz of more than 2.00 μm, preferably a roughness Rz in the range of 4 μm to 6 μm.
10. Heat-shrinkable film according to claim 9 , wherein the second polymer ply B has a roughness Rz of more than 2.00 μm, preferably a roughness Rz in the range of 4 μm to 6 μm.
11. Heat-shrinkable, un axially stretched film consisting of
a first polymer ply A which comprises at least one dark pigment and at least one white pigment; and
a second polymer ply B which comprises at least one white pigment,
wherein:
the first polymer ply A and the second polymer ply B, independently of each other, comprise one or more polymers which are selected from the group of the polyesters, polyolefins, polystyrenes and polyvinyl halides,
the film has a thickness of 20 μm to 100 μm,
the thickness ratio of the first polymer ply A to the second polymer ply B is in the range 5:95 to 50:50,
the light transmission of the fila is not more than 12%, and
the film after 15 seconds in a water bath having a temperature of 95° C. exhibits shrinkage in a main shrinking direction in the range of 20% to 85%.
12. Heat-shrinkable film according to claim 11 , wherein the second polymer ply B has an L* value of at least 85.
13. Heat-shrinkable film according to claim 11 , wherein at least one of the surfaces which face away from each other of the first polymer ply A and of the second polymer ply B is smooth.
14. Heat-shrinkable film according to claim 11 , wherein the second polymer ply B can be printed on.
15. Heat-shrinkable film according to claim 11 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polyester.
16. Heat-shrinkable film according to claim 11 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polyolefin.
17. Heat-shrinkable film according to claim 11 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polystyrene.
18. Heat-shrinkable film according to claim 11 , wherein the first polymer ply A and the second polymer ply B, independently of each other, comprise a polyvinyl halide.
19. Heat-shrinkable film according to claim 11 , wherein the second polymer ply B has a roughness Rz of more than 2.00 μm, preferably a roughness Rz in the range of 4 μm to 6 μm.
20. Heat-shrinkable film according to claim 19 , wherein the second polymer ply B has a roughness Rz of more than 2.00 μm, preferably a roughness Rz in the range of 4 μm to 6 μm.