Plasma-coated sealing element
A method includes using a sealing element to dynamically seal a sealing body in the presence of a lubricant. The sealing element has an elastomeric base body and a plasma coating. The coating includes the elements carbon, oxygen, silicon, and hydrogen. The coating has the following properties at least at the surface: the amount ratio C:Si (at %/at %) is >5, the amount ratio O:Si (at %/at %) is >3, and the surface energy is <50 mN/m. In an embodiment, the coating includes the element fluorine.
1. A method comprising:
using a sealing element to dynamically seal a sealing body in the presence of a lubricant, the sealing element having an elastomeric base body and a plasma coating,
wherein the coating comprises the elements carbon, oxygen, silicon, hydrogen,
wherein the coating has the following properties at least at the surface:
the amount ratio C:Si (at %/at %) is >5
the amount ratio O:Si (at %/at %) is >3, and
the surface energy is <50 mN/m.
2. The method according to claim 1 , wherein the proportion of Si is from 0.5 at % to 5 at % at least at the surface of the coating, and/or
wherein the proportion of C is >60 at % at least at the surface of the coating.
3. The method according to claim 1 , wherein the amount ratio C:O is >3 (at %/at %) at least at the surface of the coating.
4. The method according to claim 1 , wherein the amount ratio (at %/at %) of C:Si at least at the surface of the coating is from 10 to 80, the ratio O:Si is from 4 to 15 (at %/at %) and the ratio C:O is from 3 to 12 (at %/at %).
5. The method according to claim 1 , wherein the coating is obtainable in a plasma coating process in which a gaseous silicon precursor is used.
6. The method according to claim 1 , wherein the coating has the following proportions (in at %) at least at the surface:
Carbon:
50% to 95%
Oxygen:
5% to 25%
Silicon:
0.5% to 5%
Fluorine:
0% to 35%
7. The method according to claim 1 , wherein the elastomeric base body is a fluoroelastomer.
8. The method according to claim 1 , wherein the contact angle of the coating relative to the lubricant is from 10° to 50°.
9. The method according to claim 1 , wherein the lubricant has a kinematic viscosity of >200 mm 2 /s measured at 40° C., and/or
wherein the lubricant is a polyether, especially a polyalkylene glycol, or a polyester, or a mixture thereof.
10. The method according to claim 1 , wherein the use is carried out at an oil sump temperature <80° C.
11. The method according to claim 1 , wherein the sealing element and/or the base body is a sealing ring.
12. A sealing system comprising a sealing element, a sealing body, and an intermediate dynamic sealing gap,
wherein the sealing element has an elastomeric base body and a plasma coating,
wherein the coating comprises the elements carbon, oxygen, silicon, hydrogen,
wherein the coating has the following properties at least at the surface:
the amount ratio C:Si (at %/at %) is >5
the amount ratio O:Si (at %/at %) is >3, and
the surface energy is <50 mN/m.
13. A device comprising a sealing system according to claim 12 , especially in form of a transmission, a pump, a motor, or a motor vehicle.
14. A sealing element for dynamically sealing a sealing body in the presence of a lubricant, the sealing element having an elastomeric base body made of a fluoroelastomer and a plasma coating,
wherein the coating comprises the elements carbon, oxygen, silicon, and hydrogen,
wherein the coating has the following properties at least at the surface:
the amount ratio C:Si (at %/at %) is >5
the amount ratio O:Si (at %/at %) is >3, and
the surface energy is <50 mN/m.
15. A method for producing the sealing element according to claim 14 by plasma-assisted vapor deposition, the method comprising the steps of:
(a) introducing the elastomeric base body into the plasma device,
(b) introducing at least one gaseous silicon precursor into the device, and
(c) coating the base body in the device.
16. The method according to claim 1 , wherein the coating comprises the element fluorine.
17. The method according to claim 1 , wherein the coating has the following proportions (in at %) at least at the surface:
Carbon:
60% to 90%
Oxygen:
9% to 18%
Silicon:
1% to 4%
Fluorine:
0% to 25%
18. The method according to claim 8 , wherein the contact angle of the coating relative to the lubricant is from 15° to 30°.
19. The sealing system according to claim 12 , further comprising a lubricant.
20. The sealing element according to claim 14 , wherein the coating comprises the element fluorine.