Coated fabric for airbag
The purpose of the present invention pertains to a coated fabric used for an automotive airbag, and more particularly, a coated fabric for an airbag most suitable for a rollover curtain airbag which is produced applying a sealing agent to a coated fabric and sewing the resulting fabric and which can keep the adhesion of the sealing agent to the coat resin even after long-term and high-temperature aging. The present coated fabric for an airbag is obtained by applying an addition-polymerizable solvent-free silicone resin onto at least one surface of a synthetic fiber textile, wherein a coating amount of the silicone resin is 15 to 45 g/m 2 ; and a weft strain/warp strain ratio as observed in stretching the coated fabric is 0.30 to 0.65.
1. A coated fabric for an airbag, comprising a synthetic fiber textile and an addition-polymerized silicone resin on at least one surface of the synthetic fiber textile,
wherein the coated fabric is obtained by a method including applying a silicone resin having a resin viscosity of 5000 to 40000 mPa·sec onto a synthetic fiber textile, while applying a tensile force of 400 to 1000 N/m in a traveling direction to the synthetic fiber textile; and
wherein the coated fabric has a coating amount of the silicone resin of 24 to 45 g/m 2 , an average resin thickness of warp and weft at a vertex portion on the surface of the coated fabric of 4 μm or more and 25 μm or less, and an average ratio of strain of the coated fabric in weft direction to strain of the coated fabric in warp direction of 0.30 to 0.65 as observed in stretching the coated fabric in the warp direction.
2. The coated fabric for an airbag according to claim 1 , wherein an average resin thickness of warp and weft at a vertex portion on the surface of the coated fabric is 6 μm or more.
3. The coated fabric for an airbag according to claim 1 , wherein a difference in the bending resistance between in warp direction and in weft direction of the coated fabric is 3 to 20 mm.
4. The coated fabric for an airbag according to claim 1 , wherein a total fineness of a yarn constituting the textile is 200 to 550 dtex.
5. The coated fabric for an airbag according to claim 1 , wherein a cover factor of the textile is 1800 to 2500.
6. The coated fabric for an airbag according to claim 2 , wherein a difference in the bending resistance between in warp direction and in weft direction of the coated fabric is 3 to 20 mm.
7. The coated fabric for an airbag according to claim 2 , wherein a total fineness of a yarn constituting the textile is 200 to 550 dtex.
8. The coated fabric for an airbag according to claim 3 , wherein a total fineness of a yarn constituting the textile is 200 to 550 dtex.
9. The coated fabric for an airbag according to claim 6 , wherein a total fineness of a yarn constituting the textile is 200 to 550 dtex.
10. The coated fabric for an airbag according to claim 2 , wherein a cover factor of the textile is 1800 to 2500.
11. The coated fabric for an airbag according to claim 3 , wherein a cover factor of the textile is 1800 to 2500.
12. The coated fabric for an airbag according to claim 4 , wherein a cover factor of the textile is 1800 to 2500.
13. The coated fabric for an airbag according to claim 6 , wherein a cover factor of the textile is 1800 to 2500.
14. The coated fabric for an airbag according to claim 7 , wherein a cover factor of the textile is 1800 to 2500.
15. The coated fabric for an airbag according to claim 8 , wherein a cover factor of the textile is 1800 to 2500.
16. The coated fabric for an airbag according to claim 9 , wherein a cover factor of the textile is 1800 to 2500.