Disclosed is a post-processing method for improving anti-wear and friction-reducing properties of a CrN coating. According to the method, the CrN coating is subjected to a thermal cycling treatment in a temperature range of −20° C. to 60° C. under a humidity environment of 60%-80% R.H. The post-processing method can substantially improve the anti-wear and friction-reducing properties of the CrN coating, so that friction pair parts deposited with the coating achieve a stable operation for a long time.
1. A post-processing method for CrN coating, which comprises: performing a thermal cycle treatment on the CrN coating in a temperature range of −20° C. to 60° C. under a humidity environment of 60% to 80% R.H,
wherein, in the thermal cycle treatment, a single thermal cycle comprises a heating process from −20° C. to 60° C. and a cooling process from 60° C. to −20° C., a single thermal cycle time is 2 h, every 6 single thermal cycles is one period, a constant temperature is maintained between every two periods for 12 h, and the constant temperature has a fluctuation of ±0.5° C.,
in the heating process, a heating rate is 2° C/min and a temperature deviation is less than or equal to ±2° C; and
in the cooling process, a cooling rate is 1° C/min and a temperature deviation is less than or equal to ±2° C.
2. The post-processing method of claim 1 , wherein the humidity has a deviation of less than or equal to ±2% R.H.
3. The post-processing method of claim 1 , wherein the time of the thermal cycle treatment is 7 days.
4. The post-processing method of claim 1 , wherein the thickness of the CrN coating is from 2 μm to 80 μm, and the thickness deviation is less than or equal to 0.5 μm.
5. The post-processing method of claim 1 , wherein the CrN coating is plated on a substrate by a multi-arc ion plating technique, and the substrate is a metal or an alloy.
6. The post-processing method of claim 5 , wherein the substrate is a 316 L stainless steel substrate.
7. The post-processing method of claim 5 , wherein the CrN coating is plated on the substrate by multi-arc ion plating technology for 2 h to 24 h and then subjected to the thermal cycle treatment in the temperature range of −20° C. to 60° C., wherein the temperature deviation is less than or equal to ±2° C.
8. The post-processing method of claim 6 , wherein the CrN coating is plated on the 316 L stainless steel substrate by multi-arc ion plating technology for 2 h to 24 h and then subjected to the thermal cycle treatment in the temperature range of −20° C. to 60° C., wherein the temperature deviation is less than or equal to ±2° C.